Intergranular Stress Corrosion Crack Growth of Sensitized Type 304 Stainless Steel in a Simulated Boiling-Water Reactor Environment: Fid-Bau Portal

Intergranular Stress Corrosion Crack Growth of Sensitized Type 304 Stainless Steel in a Simulated Boiling-Water Reactor Environment

Kikuchi, E. / Itow, M. / Kuniya, J. / Sakamoto, H. / Yamamoto, M. / Sudo, A. / Suzuki, S. / Kitamura, M.

Zugriff

Zugriff über TIB

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Intergranular Stress Corrosion Crack Growth of Sensitized Type 304 Stainless Steel in a Simulated Boiling-Water Reactor Environment

Kikuchi, E. / Itow, M. / Kuniya, J. / Sakamoto, H. / Yamamoto, M. / Sudo, A. / Suzuki, S. / Kitamura, M.

Intergranular Stress Corrosion Crack Growth of Sensitized Type 304 Stainless Steel in a Simulated Boiling-Water Reactor Environment

Kikuchi, E. / Itow, M. / Kuniya, J. / Sakamoto, H. / Yamamoto, M. / Sudo, A. / Suzuki, S. / Kitamura, M.

Zugriff

Zugriff über TIB

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

Intergranular Stress Corrosion Crack Growth of Sensitized Type 304 Stainless Steel in a Simulated Boiling-Water Reactor Environment

Beteiligte:

Kikuchi, E. (Autor:in) / Itow, M. (Autor:in) / Kuniya, J. (Autor:in) / Sakamoto, H. (Autor:in) / Yamamoto, M. (Autor:in) / Sudo, A. (Autor:in) / Suzuki, S. (Autor:in) / Kitamura, M. (Autor:in)

Erschienen in:

CORROSION -HOUSTON TX- ; 53 ; 306-311

Erscheinungsdatum:

01.01.1997

Format / Umfang:

6 pages

ISSN:

0010-9312

Medientyp:

Aufsatz (Zeitschrift)

Format:

Sprache:

Englisch

Klassifikation:

DDC: 620.11223

Saito, N. / Kikuchi, E. / Sakamoto, H. et al. | British Library Online Contents | 1997

Fatigue Crack Growth Behavior of Sensitized Type 304 Stainless Steel Under Boiling Water Reactor Conditions

Chen, Y. Y. / Shih, H. C. / Wang, L. H. et al. | British Library Online Contents | 2007

Effect of Low-Temperature Sensitization on Intergranular Stress Corrosion Cracking Behavior of Austenitic Stainless Steels in Simulated Boiling Water Reactor Environment

Bali, S.C. / Kain, V. / Raja, V.S. | British Library Online Contents | 2009

Accelerated test for evaluation of intergranular stress corrosion cracking initiation characteristics of non-sensitized 316 austenitic stainless steel in simulated pressure water reactor environment

Zhong, Xiangyu / Bali, Shirish Chandrakant / Shoji, Tetsuo | British Library Online Contents | 2017

Stress Corrosion Cracking Crack Growth Behavior of Type 316L Stainless Steel Weld Metals in Boiling Water Reactor Environments

Kim, J.H. / Ballinger, R.G. | British Library Online Contents | 2008

Nach oben