Behavior of Mg-15Gd-5Y-0.5Zr alloy during solution heat treatment from 500 to 540degreeC

Gao, Y. / Wang, Q. / Gu, J. / Zhao, Y. / Tong, Y.

Zugriff

Zugriff über TIB

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Behavior of Mg-15Gd-5Y-0.5Zr alloy during solution heat treatment from 500 to 540degreeC

Gao, Y. / Wang, Q. / Gu, J. / Zhao, Y. / Tong, Y.

Behavior of Mg-15Gd-5Y-0.5Zr alloy during solution heat treatment from 500 to 540degreeC

Gao, Y. / Wang, Q. / Gu, J. / Zhao, Y. / Tong, Y.

Zugriff

Zugriff über TIB

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

Behavior of Mg-15Gd-5Y-0.5Zr alloy during solution heat treatment from 500 to 540degreeC

Beteiligte:

Gao, Y. (Autor:in) / Wang, Q. (Autor:in) / Gu, J. (Autor:in) / Zhao, Y. (Autor:in) / Tong, Y. (Autor:in)

Erschienen in:

MATERIALS SCIENCE AND ENGINEERING A ; 459 ; 117-123

Erscheinungsdatum:

01.01.2007

Format / Umfang:

7 pages

ISSN:

0921-5093

Medientyp:

Aufsatz (Zeitschrift)

Format:

Sprache:

Englisch

Klassifikation:

DDC: 620.11

Gao, X. / He, S. M. / Zeng, X. Q. et al. | British Library Online Contents | 2006

Behavior of Zr-Rich Phase in a Cast NiAl-33.5Cr-0.5Zr Alloy during Heat Treatment

Li, H. / Guo, J. / Lai, W. et al. | British Library Online Contents | 2001

Characterization of phases in Mg-4Y-4Sm-0.5Zr alloy processed by heat treatment

Li, D. / Wang, Q. / Ding, W. | British Library Online Contents | 2006

Tensile crack initiation behavior of cast Mg–3Nd–0.2Zn–0.5Zr magnesium alloy

Yue, Haiyan / Fu, Penghuai / Li, Zhenming et al. | British Library Online Contents | 2016

Tensile crack initiation behavior of cast Mg–3Nd–0.2Zn–0.5Zr magnesium alloy

Yue, H. / Fu, P. / Li, Z. et al. | British Library Online Contents | 2016

Nach oben