Influence of the applied stress rate on the stress corrosion cracking of 4340 and 3.5NiCrMoV steels under conditions of cathodic hydrogen charging: Fid-Bau Portal

Influence of the applied stress rate on the stress corrosion cracking of 4340 and 3.5NiCrMoV steels under conditions of cathodic hydrogen charging

Ramamurthy, S. / Lau, W. M. / Atrens, A.

Zugriff

Zugriff über TIB

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Influence of the applied stress rate on the stress corrosion cracking of 4340 and 3.5NiCrMoV steels under conditions of cathodic hydrogen charging

Ramamurthy, S. / Lau, W. M. / Atrens, A.

Influence of the applied stress rate on the stress corrosion cracking of 4340 and 3.5NiCrMoV steels under conditions of cathodic hydrogen charging

Ramamurthy, S. / Lau, W. M. / Atrens, A.

Zugriff

Zugriff über TIB

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

Influence of the applied stress rate on the stress corrosion cracking of 4340 and 3.5NiCrMoV steels under conditions of cathodic hydrogen charging

Beteiligte:

Ramamurthy, S. (Autor:in) / Lau, W. M. (Autor:in) / Atrens, A. (Autor:in)

Erschienen in:

CORROSION SCIENCE ; 53 ; 2419-2429

Erscheinungsdatum:

01.01.2011

Format / Umfang:

11 pages

ISSN:

0010-938X

Medientyp:

Aufsatz (Zeitschrift)

Format:

Sprache:

Englisch

Klassifikation:

DDC: 620.16205 / 620

Ramamurthy, S. / Atrens, A. | British Library Online Contents | 2010

The stress corrosion cracking of as-quenched 4340 and 3.5NiCrMoV steels under stress rate control in distilled water at 90C

Ramamurthy, S. / Atrens, A. | British Library Online Contents | 1993

Environmental effects on the stress corrosion cracking susceptibility of 3.5NiCrMoV steels in high temperature water

Maeng, W. Y. / Lee, J. H. / Kim, U. C. | British Library Online Contents | 2005

The effect of acetic acid on the stress corrosion cracking of 3.5NiCrMoV turbine steels in high temperature water

Maeng, W. Y. / Macdonald, D. D. | British Library Online Contents | 2008

The influence of hydrogen on 3.5NiCrMoV steel studied using the linearly increasing stress test

Liu, Q. / Irwanto, B. / Atrens, A. | British Library Online Contents | 2012

Nach oben