X-ray diffraction study of microstructural changes during fatigue damage initiation in pipe steels: Role of the initial dislocation structure: Fid-Bau Portal

X-ray diffraction study of microstructural changes during fatigue damage initiation in pipe steels: Role of the initial dislocation structure

Pinheiro, B. / Lesage, J. / Pasqualino, I. / Bemporad, E. / Benseddiq, N.

Zugriff

Zugriff über TIB

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

X-ray diffraction study of microstructural changes during fatigue damage initiation in pipe steels: Role of the initial dislocation structure

Pinheiro, B. / Lesage, J. / Pasqualino, I. / Bemporad, E. / Benseddiq, N.

X-ray diffraction study of microstructural changes during fatigue damage initiation in pipe steels: Role of the initial dislocation structure

Pinheiro, B. / Lesage, J. / Pasqualino, I. / Bemporad, E. / Benseddiq, N.

Zugriff

Zugriff über TIB

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

X-ray diffraction study of microstructural changes during fatigue damage initiation in pipe steels: Role of the initial dislocation structure

Beteiligte:

Pinheiro, B. (Autor:in) / Lesage, J. (Autor:in) / Pasqualino, I. (Autor:in) / Bemporad, E. (Autor:in) / Benseddiq, N. (Autor:in)

Erschienen in:

MATERIALS SCIENCE AND ENGINEERING A ; 580 ; 1-12

Erscheinungsdatum:

01.01.2013

Format / Umfang:

12 pages

ISSN:

0921-5093

Medientyp:

Aufsatz (Zeitschrift)

Format:

Sprache:

Englisch

Klassifikation:

DDC: 620.11

Pinheiro, B. / Lesage, J. / Pasqualino, I. et al. | British Library Online Contents | 2012

Influential microstructural changes on rolling contact fatigue crack initiation in pearlitic rail steels

Eden, H. C. / Garnham, J. E. / Davis, C. L. | British Library Online Contents | 2005

Void initiation and microstructural changes during wire drawing of pearlitic steels

Nam, W. J. / Bae, C. M. | British Library Online Contents | 1995

Dislocation Dipole Models for Fatigue Crack Initiation

T. Mura / K. Tanaka | NTIS | 1981

Microstructural fatigue mechanisms: Cyclic slip irreversibility, crack initiation, non-linear elastic damage analysis

Mughrabi, H. | British Library Online Contents | 2013

Nach oben