Mechanical Properties and Microstructural Changes in EVA Polymer Mortar Exposed to Elevated Temperature
https://orcid.org/0000-0003-2339-7971
https://orcid.org/0000-0002-3102-1520
https://orcid.org/0000-0002-8093-1942
The contribution of ethylene vinyl acetate (EVA) to enhancing cement properties, especially in terms of thermal stability and microstructural changes under elevated temperatures, has not been fully clarified. This research conducted comprehensive experiments to determine the heat-induced damage of EVA mortar and contrasted it with the control group subjected to high temperatures. The results indicate that EVA improves mortar’s resistance to heat-induced degradation through gasification and decomposition processes. Notably, a strong correlation between compressive strength and ultrasonic pulse velocity (UPV) is observed. Moreover, the new phase existence of calcium acetate (CA) further reveals EVA’s active participation in the cement hydration, increasing the content of ettringite (AFt) and calcium hydroxide (CH). Finally, microscopic analysis reveals voids formation due to calcium silicate hydrate (C-S-H) dehydrates after high thermal treatment. This research offers valuable insights for the utilization of EVA in construction projects subjected to elevated temperatures.
Mechanical Properties and Microstructural Changes in EVA Polymer Mortar Exposed to Elevated Temperature
https://orcid.org/0000-0003-2339-7971
https://orcid.org/0000-0002-3102-1520
https://orcid.org/0000-0002-8093-1942
The contribution of ethylene vinyl acetate (EVA) to enhancing cement properties, especially in terms of thermal stability and microstructural changes under elevated temperatures, has not been fully clarified. This research conducted comprehensive experiments to determine the heat-induced damage of EVA mortar and contrasted it with the control group subjected to high temperatures. The results indicate that EVA improves mortar’s resistance to heat-induced degradation through gasification and decomposition processes. Notably, a strong correlation between compressive strength and ultrasonic pulse velocity (UPV) is observed. Moreover, the new phase existence of calcium acetate (CA) further reveals EVA’s active participation in the cement hydration, increasing the content of ettringite (AFt) and calcium hydroxide (CH). Finally, microscopic analysis reveals voids formation due to calcium silicate hydrate (C-S-H) dehydrates after high thermal treatment. This research offers valuable insights for the utilization of EVA in construction projects subjected to elevated temperatures.
Mechanical Properties and Microstructural Changes in EVA Polymer Mortar Exposed to Elevated Temperature
https://orcid.org/0000-0003-2339-7971
https://orcid.org/0000-0002-3102-1520
https://orcid.org/0000-0002-8093-1942
The contribution of ethylene vinyl acetate (EVA) to enhancing cement properties, especially in terms of thermal stability and microstructural changes under elevated temperatures, has not been fully clarified. This research conducted comprehensive experiments to determine the heat-induced damage of EVA mortar and contrasted it with the control group subjected to high temperatures. The results indicate that EVA improves mortar’s resistance to heat-induced degradation through gasification and decomposition processes. Notably, a strong correlation between compressive strength and ultrasonic pulse velocity (UPV) is observed. Moreover, the new phase existence of calcium acetate (CA) further reveals EVA’s active participation in the cement hydration, increasing the content of ettringite (AFt) and calcium hydroxide (CH). Finally, microscopic analysis reveals voids formation due to calcium silicate hydrate (C-S-H) dehydrates after high thermal treatment. This research offers valuable insights for the utilization of EVA in construction projects subjected to elevated temperatures.
Mechanical Properties and Microstructural Changes in EVA Polymer Mortar Exposed to Elevated Temperature
J. Mater. Civ. Eng.
Cai, Runze (Autor:in) / Mao, Jize (Autor:in) / Kurumisawa, Kiyofumi (Autor:in) / Shi, Gang (Autor:in)
01.01.2025
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Effect of elevated temperature on physico-mechanical properties of metakaolin blended cement mortar
| British Library Online Contents | 2009
Effect of Elevated Temperature on Physico-Mechanical Properties of Metakaolin Blended Cement Mortar
| British Library Conference Proceedings | 2007
Aggregate Type Influence on Microstructural Behavior of Concrete Exposed to Elevated Temperature
| DOAJ | 2022
Microstructural changes caused by carbonation of cement mortar
| Tema Archiv | 2001