Synergistic Effect of Early-Strength Agents on the Mechanical Strength of Alkali-Free Liquid Accelerator Mortar

Wu, Zhihong / Zhang, Wan / Huang, Wang / Pan, Yuexin / Wang, Jiawei / Zhou, Huafeng / Li, Zhishun

As the core admixture of shotcrete, the accelerator promotes the rapid setting of shotcrete. In order to promote the rapid development of strength, the synergistic effect and the synergistic mechanism of early-strength agents [ $Al ({NO}_{3})_{3}$ (AN), and $Mg ({NO}_{3})_{2}$ (MN)], and aluminum sulfate liquid accelerator on the strength of mortar were investigated. The aluminum sulfate liquid accelerator used in this paper was named AF. The results show that the 1-day strength of the mortar reached 8.8 and 10.73 MPa when AF was added with 2.4% AN and 1.8% MN, respectively. When AF and 2.4% AN were used, the initial and final setting times of the cement paste were 1 min 32 s and 3 min 50 s, respectively, whereas the AF and a very small amount of MN would prolong the setting time of the paste. The synergistic mechanism of AN/MN and AF is as follows: AF provides a large amount of ${SO}_{4}^{2 -}$ and ${Al}^{3 +}$ , which promotes the rapid formation of ettringite (AFt). In addition, ${NO}_{3}^{-}$ in AN and MN promotes the formation of the AFt phase $3 CaO \cdot {Al}_{2} O_{3} \cdot Ca ({NO}_{3})_{2} \cdot {XH}_{2} O$ ( ${NO}_{3} - AFt$ ). Compared with AN, ${Mg}^{2 +}$ dissolved by MN will first precipitate $Mg (OH)_{2}$ with ${OH}^{-}$ , providing crystal nuclei for the hydration system and accelerating the hydration of $C_{3} S$ . It is concluded that AF and MN have a better synergistic effect on improving early strength.

Zugriff

Zugriff prüfen

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Synergistic Effect of Early-Strength Agents on the Mechanical Strength of Alkali-Free Liquid Accelerator Mortar

Wu, Zhihong / Zhang, Wan / Huang, Wang / Pan, Yuexin / Wang, Jiawei / Zhou, Huafeng / Li, Zhishun

As the core admixture of shotcrete, the accelerator promotes the rapid setting of shotcrete. In order to promote the rapid development of strength, the synergistic effect and the synergistic mechanism of early-strength agents [ $Al ({NO}_{3})_{3}$ (AN), and $Mg ({NO}_{3})_{2}$ (MN)], and aluminum sulfate liquid accelerator on the strength of mortar were investigated. The aluminum sulfate liquid accelerator used in this paper was named AF. The results show that the 1-day strength of the mortar reached 8.8 and 10.73 MPa when AF was added with 2.4% AN and 1.8% MN, respectively. When AF and 2.4% AN were used, the initial and final setting times of the cement paste were 1 min 32 s and 3 min 50 s, respectively, whereas the AF and a very small amount of MN would prolong the setting time of the paste. The synergistic mechanism of AN/MN and AF is as follows: AF provides a large amount of ${SO}_{4}^{2 -}$ and ${Al}^{3 +}$ , which promotes the rapid formation of ettringite (AFt). In addition, ${NO}_{3}^{-}$ in AN and MN promotes the formation of the AFt phase $3 CaO \cdot {Al}_{2} O_{3} \cdot Ca ({NO}_{3})_{2} \cdot {XH}_{2} O$ ( ${NO}_{3} - AFt$ ). Compared with AN, ${Mg}^{2 +}$ dissolved by MN will first precipitate $Mg (OH)_{2}$ with ${OH}^{-}$ , providing crystal nuclei for the hydration system and accelerating the hydration of $C_{3} S$ . It is concluded that AF and MN have a better synergistic effect on improving early strength.

Synergistic Effect of Early-Strength Agents on the Mechanical Strength of Alkali-Free Liquid Accelerator Mortar

Wu, Zhihong / Zhang, Wan / Huang, Wang / Pan, Yuexin / Wang, Jiawei / Zhou, Huafeng / Li, Zhishun

As the core admixture of shotcrete, the accelerator promotes the rapid setting of shotcrete. In order to promote the rapid development of strength, the synergistic effect and the synergistic mechanism of early-strength agents [ $Al ({NO}_{3})_{3}$ (AN), and $Mg ({NO}_{3})_{2}$ (MN)], and aluminum sulfate liquid accelerator on the strength of mortar were investigated. The aluminum sulfate liquid accelerator used in this paper was named AF. The results show that the 1-day strength of the mortar reached 8.8 and 10.73 MPa when AF was added with 2.4% AN and 1.8% MN, respectively. When AF and 2.4% AN were used, the initial and final setting times of the cement paste were 1 min 32 s and 3 min 50 s, respectively, whereas the AF and a very small amount of MN would prolong the setting time of the paste. The synergistic mechanism of AN/MN and AF is as follows: AF provides a large amount of ${SO}_{4}^{2 -}$ and ${Al}^{3 +}$ , which promotes the rapid formation of ettringite (AFt). In addition, ${NO}_{3}^{-}$ in AN and MN promotes the formation of the AFt phase $3 CaO \cdot {Al}_{2} O_{3} \cdot Ca ({NO}_{3})_{2} \cdot {XH}_{2} O$ ( ${NO}_{3} - AFt$ ). Compared with AN, ${Mg}^{2 +}$ dissolved by MN will first precipitate $Mg (OH)_{2}$ with ${OH}^{-}$ , providing crystal nuclei for the hydration system and accelerating the hydration of $C_{3} S$ . It is concluded that AF and MN have a better synergistic effect on improving early strength.

Zugriff

Zugriff prüfen

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

Synergistic Effect of Early-Strength Agents on the Mechanical Strength of Alkali-Free Liquid Accelerator Mortar

Weitere Titelangaben:

J. Mater. Civ. Eng.

Beteiligte:

Wu, Zhihong (Autor:in) / Zhang, Wan (Autor:in) / Huang, Wang (Autor:in) / Pan, Yuexin (Autor:in) / Wang, Jiawei (Autor:in) / Zhou, Huafeng (Autor:in) / Li, Zhishun (Autor:in)

Erschienen in:

Journal of Materials in Civil Engineering ; 36

Erscheinungsdatum:

01.07.2024

ISSN:

1943-5533 , 0899-1561

DOI:

https://doi.org/10.1061/JMCEE7.MTENG-17411

Medientyp:

Aufsatz (Zeitschrift)

Format:

Elektronische Ressource

Sprache:

Englisch

Schlagwörter:

Early-strength agent , Dual-ion effect , Synergistic mechanism , Alkali-free liquid accelerator

Ähnliche Titel

High-early-strength alkali-free liquid accelerator and preparation method thereof

LIU JIANJUN / YANG YANG | Europäisches Patentamt | 2021

Freier Zugriff

Quick-setting high-strength alkali-free liquid accelerator

LI XIAONING / YAN CHAOQIANG / HAO LIGUO et al. | Europäisches Patentamt | 2020

Freier Zugriff

Alkali-free accelerator for early high-strength sprayed concrete

ZHANG HAITAO / XU WEIXING | Europäisches Patentamt | 2023

Freier Zugriff

Preparation method of early-strength high-efficiency alkali-free accelerator

CHEN JIE / GAO JIAHONG / FANG SHICHANG et al. | Europäisches Patentamt | 2020

Freier Zugriff

METHOD FOR PREPARING EARLY-STRENGTH LIQUID ACCELERATOR FREE OF ALKALI, CHLORINE, AND FLUORINE

YUAN QIANG / TIAN YI / YANG QIAN et al. | Europäisches Patentamt | 2024

Freier Zugriff