Self-Cleaning Performance of Basalt Fiber–Reinforced GGBS-Based Geopolymer Mortar Containing Nano ${TiO}_{2}$

Tanyildizi, Harun / Yilmaz, Atilla / Açik, Volkan / Demirelli, Kadir

This study examined the self-cleaning and mechanical properties of basalt fiber–reinforced ground granulated blast furnace slag (GGBS)-based geopolymer mortar containing nano ${TiO}_{2}$ . The nano ${TiO}_{2}$ and basalt fiber in mixtures were used at 0%, 0.25%, 0.5%, and 1% by weight of GGBS. The cubes ( $50 \times 50 \times 50 mm$ ) and prisms ( $40 \times 40 \times 160 mm$ ) samples containing nano ${TiO}_{2}$ and basalt fiber were produced and cured in the oven for 24 h at 60°C. Then, these samples were kept at room temperature at $23 ° C \pm 2 ° C$ for 28 days. Lastly, the compressive strength, flexural strength, ultrasonic pulse velocity, capillary water absorption, and self-cleaning tests of GGBS-based geopolymer mortars were carried out. In this study, the Rhodamine-B test was used to determine self-cleaning. This study showed that the compressive strength, flexural strength, and ultrasonic pulse velocity values of the GGBS-based geopolymer mortars increased as the nano ${TiO}_{2}$ and basalt fiber ratios increased, but their capillary water absorption coefficient decreased. Also, this study found that the self-cleaning rate of GGBS-based geopolymer mortars containing 1% nano ${TiO}_{2}$ was obtained as 50.62% at 28 days.

Zugriff

Zugriff prüfen

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Self-Cleaning Performance of Basalt Fiber–Reinforced GGBS-Based Geopolymer Mortar Containing Nano ${TiO}_{2}$

Tanyildizi, Harun / Yilmaz, Atilla / Açik, Volkan / Demirelli, Kadir

This study examined the self-cleaning and mechanical properties of basalt fiber–reinforced ground granulated blast furnace slag (GGBS)-based geopolymer mortar containing nano ${TiO}_{2}$ . The nano ${TiO}_{2}$ and basalt fiber in mixtures were used at 0%, 0.25%, 0.5%, and 1% by weight of GGBS. The cubes ( $50 \times 50 \times 50 mm$ ) and prisms ( $40 \times 40 \times 160 mm$ ) samples containing nano ${TiO}_{2}$ and basalt fiber were produced and cured in the oven for 24 h at 60°C. Then, these samples were kept at room temperature at $23 ° C \pm 2 ° C$ for 28 days. Lastly, the compressive strength, flexural strength, ultrasonic pulse velocity, capillary water absorption, and self-cleaning tests of GGBS-based geopolymer mortars were carried out. In this study, the Rhodamine-B test was used to determine self-cleaning. This study showed that the compressive strength, flexural strength, and ultrasonic pulse velocity values of the GGBS-based geopolymer mortars increased as the nano ${TiO}_{2}$ and basalt fiber ratios increased, but their capillary water absorption coefficient decreased. Also, this study found that the self-cleaning rate of GGBS-based geopolymer mortars containing 1% nano ${TiO}_{2}$ was obtained as 50.62% at 28 days.

Self-Cleaning Performance of Basalt Fiber–Reinforced GGBS-Based Geopolymer Mortar Containing Nano ${TiO}_{2}$

Tanyildizi, Harun / Yilmaz, Atilla / Açik, Volkan / Demirelli, Kadir

This study examined the self-cleaning and mechanical properties of basalt fiber–reinforced ground granulated blast furnace slag (GGBS)-based geopolymer mortar containing nano ${TiO}_{2}$ . The nano ${TiO}_{2}$ and basalt fiber in mixtures were used at 0%, 0.25%, 0.5%, and 1% by weight of GGBS. The cubes ( $50 \times 50 \times 50 mm$ ) and prisms ( $40 \times 40 \times 160 mm$ ) samples containing nano ${TiO}_{2}$ and basalt fiber were produced and cured in the oven for 24 h at 60°C. Then, these samples were kept at room temperature at $23 ° C \pm 2 ° C$ for 28 days. Lastly, the compressive strength, flexural strength, ultrasonic pulse velocity, capillary water absorption, and self-cleaning tests of GGBS-based geopolymer mortars were carried out. In this study, the Rhodamine-B test was used to determine self-cleaning. This study showed that the compressive strength, flexural strength, and ultrasonic pulse velocity values of the GGBS-based geopolymer mortars increased as the nano ${TiO}_{2}$ and basalt fiber ratios increased, but their capillary water absorption coefficient decreased. Also, this study found that the self-cleaning rate of GGBS-based geopolymer mortars containing 1% nano ${TiO}_{2}$ was obtained as 50.62% at 28 days.

Zugriff

Zugriff prüfen

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

Self-Cleaning Performance of Basalt Fiber–Reinforced GGBS-Based Geopolymer Mortar Containing Nano ${TiO}_{2}$

Weitere Titelangaben:

J. Mater. Civ. Eng.

Beteiligte:

Tanyildizi, Harun (Autor:in) / Yilmaz, Atilla (Autor:in) / Açik, Volkan (Autor:in) / Demirelli, Kadir (Autor:in)

Erschienen in:

Journal of Materials in Civil Engineering ; 36

Erscheinungsdatum:

01.08.2024

ISSN:

1943-5533 , 0899-1561

DOI:

https://doi.org/10.1061/JMCEE7.MTENG-17155

Medientyp:

Aufsatz (Zeitschrift)

Format:

Elektronische Ressource

Sprache:

Englisch

Schlagwörter:

Cost analysis , Mechanical properties , Nano TiO2 , Basalt fiber , Ground granulated blast furnace slag (GGBS)-based geopolymer mortar , Self-cleaning

Ähnliche Titel

Performance Studies on Steel Fiber–Reinforced GGBS-Dolomite Geopolymer Concrete

Saranya, P. / Nagarajan, Praveen / Shashikala, Aikot Pallikkara | ASCE | 2020

Optimising GGBS-based ultra high-performance geopolymer mortar: an orthogonal array approach

Alameri, Mohammad / Joseph, Jovan / Mohamed Ali, M.S. et al. | Taylor & Francis Verlag | 2025

Freier Zugriff

Strength Behavior of Polypropylene Fiber Reinforced GGBS Based Geopolymer Clay Blends

Nagaraju, T. V. / Sharmila, Ch. Sarada / Santhoshi, A. S. P. V. | TIBKAT | 2022

Strength Behavior of Polypropylene Fiber Reinforced GGBS Based Geopolymer Clay Blends

Nagaraju, T. V. / Sharmila, Ch. Sarada / Santhoshi, A. S. P. V. | Springer Verlag | 2021

Basalt fiber reinforced geopolymer and preparation method thereof

WU ZHENGGUANG / ZHANG CONG / LOU KEKE et al. | Europäisches Patentamt | 2021

Freier Zugriff