Carbon Dioxide–Activated Steel Slag for Slag-Bonded Wallboard Application

Shao, Yixin / El-Baghdadi, Ahmed / He, Zhen / Mucci, Alfonso / Fournier, Benoit

The feasibility of making slag-bonded construction wallboard through carbon dioxide activation of steel slag was investigated. The steel slag used in the study is a by-product of the Klockner Oxygen Blown Maxhutte (KOBM) steel-making process. The ${CO}_{2}$ -activated steel slag can potentially be used as a cementing material in place of ordinary portland cement (OPC). The 2-h carbonation strength of the activated steel slag reached 46 MPa and the 28-day strength after carbonation and hydration was more than 60 MPa. Carbonation of steel slag enabled ${CO}_{2}$ utilization up to 6.8% on a dry-slag-mass basis. The high early strength obtained in ${CO}_{2}$ -activated slag is attributed to the rapid formation of calcium-silicate-hydrates and calcium carbonates. The precipitation of rhombohedral ${CaCO}_{3}$ nanoparticles significantly enhances packing density and reduces the porosity of the carbonate matrix. A slag-bonded wallboard using sawdust as lightweight filler was successfully fabricated and its mechanical performance was comparable to cement-based commercial products.

Zugriff

Zugriff prüfen

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Carbon Dioxide–Activated Steel Slag for Slag-Bonded Wallboard Application

Shao, Yixin / El-Baghdadi, Ahmed / He, Zhen / Mucci, Alfonso / Fournier, Benoit

The feasibility of making slag-bonded construction wallboard through carbon dioxide activation of steel slag was investigated. The steel slag used in the study is a by-product of the Klockner Oxygen Blown Maxhutte (KOBM) steel-making process. The ${CO}_{2}$ -activated steel slag can potentially be used as a cementing material in place of ordinary portland cement (OPC). The 2-h carbonation strength of the activated steel slag reached 46 MPa and the 28-day strength after carbonation and hydration was more than 60 MPa. Carbonation of steel slag enabled ${CO}_{2}$ utilization up to 6.8% on a dry-slag-mass basis. The high early strength obtained in ${CO}_{2}$ -activated slag is attributed to the rapid formation of calcium-silicate-hydrates and calcium carbonates. The precipitation of rhombohedral ${CaCO}_{3}$ nanoparticles significantly enhances packing density and reduces the porosity of the carbonate matrix. A slag-bonded wallboard using sawdust as lightweight filler was successfully fabricated and its mechanical performance was comparable to cement-based commercial products.

Carbon Dioxide–Activated Steel Slag for Slag-Bonded Wallboard Application

Shao, Yixin / El-Baghdadi, Ahmed / He, Zhen / Mucci, Alfonso / Fournier, Benoit

The feasibility of making slag-bonded construction wallboard through carbon dioxide activation of steel slag was investigated. The steel slag used in the study is a by-product of the Klockner Oxygen Blown Maxhutte (KOBM) steel-making process. The ${CO}_{2}$ -activated steel slag can potentially be used as a cementing material in place of ordinary portland cement (OPC). The 2-h carbonation strength of the activated steel slag reached 46 MPa and the 28-day strength after carbonation and hydration was more than 60 MPa. Carbonation of steel slag enabled ${CO}_{2}$ utilization up to 6.8% on a dry-slag-mass basis. The high early strength obtained in ${CO}_{2}$ -activated slag is attributed to the rapid formation of calcium-silicate-hydrates and calcium carbonates. The precipitation of rhombohedral ${CaCO}_{3}$ nanoparticles significantly enhances packing density and reduces the porosity of the carbonate matrix. A slag-bonded wallboard using sawdust as lightweight filler was successfully fabricated and its mechanical performance was comparable to cement-based commercial products.

Zugriff

Zugriff prüfen

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

Carbon Dioxide–Activated Steel Slag for Slag-Bonded Wallboard Application

Beteiligte:

Shao, Yixin (Autor:in) / El-Baghdadi, Ahmed (Autor:in) / He, Zhen (Autor:in) / Mucci, Alfonso (Autor:in) / Fournier, Benoit (Autor:in)

Erschienen in:

Journal of Materials in Civil Engineering ; 27

Erscheinungsdatum:

14.07.2014

ISSN:

0899-1561 , 1943-5533

DOI:

https://doi.org/10.1061/(ASCE)MT.1943-5533.0001055

Medientyp:

Aufsatz (Zeitschrift)

Format:

Elektronische Ressource

Sprache:

Unbekannt

Ähnliche Titel

Carbon Dioxide–Activated Steel Slag for Slag-Bonded Wallboard Application

El-Baghdadi, Ahmed | Online Contents | 2015

Carbon Dioxide-Activated Steel Slag for Slag-Bonded Wallboard Application

Shao, Y. / El-Baghdadi, A. / He, Z. et al. | British Library Online Contents | 2015

Carbon dioxide activated ladle slag binder

Mahoutian, Mehrdad / Ghouleh, Zaid / Shao, Yixin | Elsevier | 2014

Carbon dioxide activated ladle slag binder

Mahoutian, Mehrdad | Online Contents | 2014

Carbon dioxide activated ladle slag binder

Mahoutian, M. / Ghouleh, Z. / Shao, Y. | British Library Online Contents | 2014