Effects of Stress Ratio and Banded Microstructure on Fatigue Crack Growth Behavior of HRB400 Steel Bar
This paper investigates the effects of stress ratio and microstructure on the fatigue crack growth (FCG) behavior of HRB400 steel bars widely used in concrete bridges. A constant stress–controlled FCG test with different stress ratios is performed on compact tension specimens. Test specimens are machined from rebar in two directions, i.e., cracks propagate in the radial and axial directions of the steel bar. The FCG rate versus stress intensity factor range under different stress ratios and different crack orientations are obtained. The morphology of the fracture surface and the FCG path are examined by scanning electron microscope and optical microscopy. Following this, the FCG curves, fracture characteristics, and FCG paths are compared. The experimental results show that the radial and axial crack predominantly present the transgranular and intergranular fracture mode, respectively. The material presents a higher resistance to FCG in radial orientation than that in axial direction.
Effects of Stress Ratio and Banded Microstructure on Fatigue Crack Growth Behavior of HRB400 Steel Bar
This paper investigates the effects of stress ratio and microstructure on the fatigue crack growth (FCG) behavior of HRB400 steel bars widely used in concrete bridges. A constant stress–controlled FCG test with different stress ratios is performed on compact tension specimens. Test specimens are machined from rebar in two directions, i.e., cracks propagate in the radial and axial directions of the steel bar. The FCG rate versus stress intensity factor range under different stress ratios and different crack orientations are obtained. The morphology of the fracture surface and the FCG path are examined by scanning electron microscope and optical microscopy. Following this, the FCG curves, fracture characteristics, and FCG paths are compared. The experimental results show that the radial and axial crack predominantly present the transgranular and intergranular fracture mode, respectively. The material presents a higher resistance to FCG in radial orientation than that in axial direction.
Effects of Stress Ratio and Banded Microstructure on Fatigue Crack Growth Behavior of HRB400 Steel Bar
Ma, Yafei (Autor:in) / Guo, Zhongzhao (Autor:in) / Wang, Lei (Autor:in) / Zhang, Jianren (Autor:in) / Liu, Yongming (Autor:in)
29.12.2017
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
| British Library Online Contents | 2018
High Strain Low Cycle Fatigue and Anti-Seismic Behavior of HRB400 QST Reinforced Steel Bars
| British Library Conference Proceedings | 2011
Corrosion Behavior of HRB400 Reinforcing Steel Using Cyclic Potentiodynamic Polarization Technique
| British Library Conference Proceedings | 2011