Experimental Determination of Early Age Fracture Toughness and Fracture Process Zone Size in Cement Pastes
The micro-scratch test and its analysis continue to grow in the fields of material science and engineering, particularly as it relates to materials at smaller scales being used for fracture resistance. In this study, white cement paste specimens were cast, extracted and their hydration was stopped at desired curing ages. A Rockwell probe was used to scratch the surface of the specimens to determine the fracture toughness at that age. Classical Brazilian split-cylinder tests were also performed to compliment the scratch tests. The excellent convergence of the raw data allows the increase of fracture toughness and splitting strength over time to be determined. Finally, Irwin's characteristic length, which is proportional to the fracture process zone size, is determined and shown to asymptotically reach a constant size.
Experimental Determination of Early Age Fracture Toughness and Fracture Process Zone Size in Cement Pastes
The micro-scratch test and its analysis continue to grow in the fields of material science and engineering, particularly as it relates to materials at smaller scales being used for fracture resistance. In this study, white cement paste specimens were cast, extracted and their hydration was stopped at desired curing ages. A Rockwell probe was used to scratch the surface of the specimens to determine the fracture toughness at that age. Classical Brazilian split-cylinder tests were also performed to compliment the scratch tests. The excellent convergence of the raw data allows the increase of fracture toughness and splitting strength over time to be determined. Finally, Irwin's characteristic length, which is proportional to the fracture process zone size, is determined and shown to asymptotically reach a constant size.
Experimental Determination of Early Age Fracture Toughness and Fracture Process Zone Size in Cement Pastes
Hoover, C. (Autor:in)
Ninth International Conference on Creep, Shrinkage, and Durability Mechanics (CONCREEP-9) ; 2013 ; Cambridge, Massachusetts, United States
23.09.2013
Aufsatz (Konferenz)
Elektronische Ressource
Englisch
Mechanical properties , Aging (material) , Creep , Concrete , Cement , Durability , Experimentation , Cracking , Toughness , Shrinkage
Fracture Surfaces of Cement Pastes, Rocks, and Cement/Rock Interfaces
| British Library Conference Proceedings | 1995
Fracture surfaces and compressive strength of hydrated cement pastes
| British Library Online Contents | 2012
Fracture Toughness of Portland Cement Concretes
| NTIS | 1968
Fracture surfaces and compressive strength of hydrated cement pastes
| Online Contents | 2012
Fracture Toughness of Cement-Based Materials
| Springer Verlag | 1989