The impact of wood waste ash on physical mechanical properties of concrete /
In this work is analysing the impact of wood waste bottom ash (WWBA) on the physical mechanical properties of Portland cement concrete (PCC). WWBA is a waste generated in power plants during burning forest residues to produce energy and heat. In 2019, about 19,800 tons of WWBA was generated only in Lithuania. Usually, WWBA is disposed of in landfills, only 26% of WWBA is used in the construction or maintenance of local roads, because of that it is useful to know properties of such WWBA and to analyse possibilities of using it in cement concrete. In the chemical composition of such WWBA type was fixed a big amount ~50% of CO2. It is known, that C retards cement hydration. Due to stabilisation this process, it was used in the same amounts catalyst waste from oil cracking (FCCCw), which could accelerate hydration processes. Oil refineries worldwide generate more than 800,000 tonnes of FCCCw per year, of which around 20% in Europe and it is the big problem to landfill. In the investigation the amount of Portland cement (5-20% by mass) was replaced by mentioned wastes and properties of fresh PCC (density, slump, flow diameter) and physical mechanical properties of hardened PCC (water absorption, capillary water absorption, ultrasound pulse velocity, density, compressive strength after 28 days and 2 years curing, SEM) were established. It was determined, that by increasing amount of waste (till 20%) the workability of concrete decreases, because used wastes had higher water requirement. The best results were obtained, when 5% of cement was replaced by WWBA. Then compressive strength after 28 days curing comparing to control sample decreased 8%, but after 2 years curing it increased 1%, also the capillary water absorption decreased, denser structure was formed. The obtained results of hardened PCC density, ultrasound pulse velocity and water absorption are similar to control samples.
The impact of wood waste ash on physical mechanical properties of concrete /
In this work is analysing the impact of wood waste bottom ash (WWBA) on the physical mechanical properties of Portland cement concrete (PCC). WWBA is a waste generated in power plants during burning forest residues to produce energy and heat. In 2019, about 19,800 tons of WWBA was generated only in Lithuania. Usually, WWBA is disposed of in landfills, only 26% of WWBA is used in the construction or maintenance of local roads, because of that it is useful to know properties of such WWBA and to analyse possibilities of using it in cement concrete. In the chemical composition of such WWBA type was fixed a big amount ~50% of CO2. It is known, that C retards cement hydration. Due to stabilisation this process, it was used in the same amounts catalyst waste from oil cracking (FCCCw), which could accelerate hydration processes. Oil refineries worldwide generate more than 800,000 tonnes of FCCCw per year, of which around 20% in Europe and it is the big problem to landfill. In the investigation the amount of Portland cement (5-20% by mass) was replaced by mentioned wastes and properties of fresh PCC (density, slump, flow diameter) and physical mechanical properties of hardened PCC (water absorption, capillary water absorption, ultrasound pulse velocity, density, compressive strength after 28 days and 2 years curing, SEM) were established. It was determined, that by increasing amount of waste (till 20%) the workability of concrete decreases, because used wastes had higher water requirement. The best results were obtained, when 5% of cement was replaced by WWBA. Then compressive strength after 28 days curing comparing to control sample decreased 8%, but after 2 years curing it increased 1%, also the capillary water absorption decreased, denser structure was formed. The obtained results of hardened PCC density, ultrasound pulse velocity and water absorption are similar to control samples.
The impact of wood waste ash on physical mechanical properties of concrete /
Vaičienė, Marija, (Autor:in) / Malaiškienė, Jurgita (Autor:in)
01.01.2021
IOP Conference Series: Materials Science and Engineering: 6th World Multidisciplinary Civil Engineering, Architecture: Urban Planning Symposium (WMCAUS 2021) 14th-18th June 2021, Prague, Czech Republic., Bristol : IOP Publishing Ltd, 2021, vol. 1203, art. no. 032097, p. 1-10. ; ISSN 1757-8981 ; eISSN 1757-899X
Aufsatz (Konferenz)
Elektronische Ressource
Englisch
Mechanical and physical properties of concrete containing FGD waste
| Online Contents | 2015
Mechanical and physical properties of concrete containing FGD waste
| Online Contents | 2015
Physical and mechanical properties of concretes produced with waste concrete
| Tema Archiv | 1997
Physical and Mechanical Properties of Concretes Produced with Waste Concrete
| Online Contents | 1997
Physical and Mechanical Properties of Concretes Produced with Waste Concrete
| British Library Online Contents | 1997