Mechanical behaviour at high temperature of alkali-activated aluminosilicates (geopolymers)
This study was designed to determine the effect of temperature on the mechanical strength (in both in vivo and post-exposure trials) of two alkaline cements (without OPC): (a) 100% fly ash (FA) and (b) 85% FA + 15% bauxite, the activated alkaline solution used was 85% 10-M NaOH + 15% sodium silicate. A Type I 42.5 R Portland cement was used as a control. Two series of trials were conducted: (i) in vivo trials in which bending and compressive strength, fracture toughness and modulus of elasticity were determined at different temperatures; and (ii) post-firing trials, assessing residual bending and compres-sive strength after a 1-h exposure to high temperatures and subsequent cooling. The findings showed that from 25 to 600 C, irrespective of the type of test (in vivo or post-firing), compressive mechanical strength rose, with the specimens exhibiting elastic behaviour and consequently brittle failure. At tem-peratures of over 600 C, behaviour differed depending on the type of test: (i) in the in vivo trials the high temperature induced pseudo-plastic strain and a decline in mechanical strength that did not necessarily entail specimen failure; (ii) in the post-firing trials, compressive strength rose.
Mechanical behaviour at high temperature of alkali-activated aluminosilicates (geopolymers)
This study was designed to determine the effect of temperature on the mechanical strength (in both in vivo and post-exposure trials) of two alkaline cements (without OPC): (a) 100% fly ash (FA) and (b) 85% FA + 15% bauxite, the activated alkaline solution used was 85% 10-M NaOH + 15% sodium silicate. A Type I 42.5 R Portland cement was used as a control. Two series of trials were conducted: (i) in vivo trials in which bending and compressive strength, fracture toughness and modulus of elasticity were determined at different temperatures; and (ii) post-firing trials, assessing residual bending and compres-sive strength after a 1-h exposure to high temperatures and subsequent cooling. The findings showed that from 25 to 600 C, irrespective of the type of test (in vivo or post-firing), compressive mechanical strength rose, with the specimens exhibiting elastic behaviour and consequently brittle failure. At tem-peratures of over 600 C, behaviour differed depending on the type of test: (i) in the in vivo trials the high temperature induced pseudo-plastic strain and a decline in mechanical strength that did not necessarily entail specimen failure; (ii) in the post-firing trials, compressive strength rose.
Mechanical behaviour at high temperature of alkali-activated aluminosilicates (geopolymers)
Martin Sanz, Antonia (Autor:in) / Pastor Caño, Jose Ignacio (Autor:in) / Palomo, Ángel (Autor:in) / Fernández Jiménez, A. (Autor:in)
18.03.2015
Construction and Building Materials, ISSN 0950-0618, 2015-03-18, No. 93
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
DDC:
624
Mechanical behaviour at high temperature of alkali-activated aluminosilicates
| Online Contents | 2015
Ion exchange in amorphous alkali-activated aluminosilicates: Potassium based geopolymers
| Online Contents | 2014
Alkali activated materials or geopolymers?
| British Library Online Contents | 2007
Utilisation of Alkali-Activated Aluminosilicates asFire Protecting Materials
| British Library Conference Proceedings | 2008