The goal of this investigation was to find out influence of heat treatment at low temperatures on the Lithuanian spruce wood bending strength. The influence of heating temperature and duration on the strength of spruce wood during static bending has been investigated. The tests were carried out using samples with size of 20 x 20 mm in cross-section and 300 mm in length. Density of samples varied from 460 up to 500 kg/m(3). The samples were heated at conditions close to those used during manufacturing process. Temperature was equal to T= 60, 80, 100 and 120 degrees C and heating duration was selected tau= 24, 48, 72 and 96 hours. The obtained results reveal that heating at relatively low temperatures, influences the strength of the spruce wood during bending. After the increase of both drying temperature and duration decrease of bending strength was found. The longer heating duration at lower temperatures results in less strength changes compare to those heated at higher temperatures for shorter duration. It was found that heating temperature is more significant technological parameter for spruce wood bending strength compare to those of heating duration.
Influence of heat treatment on the static bending strength of spruce wood
The goal of this investigation was to find out influence of heat treatment at low temperatures on the Lithuanian spruce wood bending strength. The influence of heating temperature and duration on the strength of spruce wood during static bending has been investigated. The tests were carried out using samples with size of 20 x 20 mm in cross-section and 300 mm in length. Density of samples varied from 460 up to 500 kg/m(3). The samples were heated at conditions close to those used during manufacturing process. Temperature was equal to T= 60, 80, 100 and 120 degrees C and heating duration was selected tau= 24, 48, 72 and 96 hours. The obtained results reveal that heating at relatively low temperatures, influences the strength of the spruce wood during bending. After the increase of both drying temperature and duration decrease of bending strength was found. The longer heating duration at lower temperatures results in less strength changes compare to those heated at higher temperatures for shorter duration. It was found that heating temperature is more significant technological parameter for spruce wood bending strength compare to those of heating duration.
Influence of heat treatment on the static bending strength of spruce wood
Fataraitė-Urbonienė, Eglė (Autor:in) / Juodeikienė, Inga (Autor:in) / Albrektas, Darius (Autor:in) / Meškauskas, Simonas (Autor:in)
01.01.2019
Materials science = Medžiagotyra, Kaunas : KTU, 2019, vol. 25, iss. 4, p. 455-459 ; ISSN 1392-1320 ; eISSN 2029-7289
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
DDC:
690
Influence of heat treatment on the static bending strength of spruce wood
| BASE | 2019
Influence of heat treatment on the static bending strength of spruce wood
| BASE | 2019
The Impact of Radiant Heat on the Flexural Strength and Impact Strength in Spruce Wood Bending
| Springer Verlag | 2020
Strength properties of black spruce wood under different treatment
| British Library Online Contents | 1996