Static strength and fatigue life of pinned hybrid titanium-composite single-lap-shear joints
Modern aircraft structures consist of a multi-material mix, dominated by high-performance composites, but also including metal alloys, e.g., for load introduction parts. This experimental research investigates the static and fatigue strength of pinned hybrid titanium-composite single-lap-shear joints. The Ti6Al4V adherend is manufactured by laser powder bed fusion. The joining is done by co-curing with the carbon fiber reinforced polymer adherend. The static tests focus on damage initiation and ultimate load, and are benchmarked by identical joints without pins. The fatigue tests focus on damage initiation and propagation. Digital image correlation is used for damage monitoring. Results show, (i) a high ratio of static ultimate failure to damage initiation load, (ii) early low-cycle damage initiation but then long high-cycle fatigue life until failure, and (iii) the crack stopping effect of the interlocking pins. Furthermore, visual joint failure analysis reveals a variety of damage modes, suggesting comprehensive testing and proper pin design.
Static strength and fatigue life of pinned hybrid titanium-composite single-lap-shear joints
Modern aircraft structures consist of a multi-material mix, dominated by high-performance composites, but also including metal alloys, e.g., for load introduction parts. This experimental research investigates the static and fatigue strength of pinned hybrid titanium-composite single-lap-shear joints. The Ti6Al4V adherend is manufactured by laser powder bed fusion. The joining is done by co-curing with the carbon fiber reinforced polymer adherend. The static tests focus on damage initiation and ultimate load, and are benchmarked by identical joints without pins. The fatigue tests focus on damage initiation and propagation. Digital image correlation is used for damage monitoring. Results show, (i) a high ratio of static ultimate failure to damage initiation load, (ii) early low-cycle damage initiation but then long high-cycle fatigue life until failure, and (iii) the crack stopping effect of the interlocking pins. Furthermore, visual joint failure analysis reveals a variety of damage modes, suggesting comprehensive testing and proper pin design.
Static strength and fatigue life of pinned hybrid titanium-composite single-lap-shear joints
Kralovec, Christoph (Autor:in) / Dengg, Andreas (Autor:in) / Schagerl, Martin (Autor:in) / Schiller, Arne (Autor:in) / Bisagni, Chiara (Autor:in) / Loebbecke, Miriam (Autor:in) / Haubrich, Jan (Autor:in) / Hanelt, Robert (Autor:in) / Kralovec, Christoph / Dengg, Andrea
01.01.2025
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Tensile Strength and Fatigue Properties of Z-Pinned Composite Lap Joints
| British Library Conference Proceedings | 2004
The strength of pinned joints in laminated composites
| British Library Online Contents | 2003
| Wiley | 2024
Elevated Temperature Properties of Pinned Composite Lap Joints
| British Library Online Contents | 2008
Static and fatigue strength of timber joints
Engineering Index Backfile | 1953