Optimized alkali-activated slag-based concrete reinforced with recycled tire steel fiber
This study employed Taguchi-Grey relational analysis to optimize the influences of binder content, the molarity of sodium hydroxide (SH) solution, alkaline solution to binder content (Al/Bi) ratio, water to alkali-activated solids (W/S) ratio, and sodium silicate to sodium hydroxide solution (SS/SH) ratio on the workability, setting time, and compressive strength of alkali-activated slag-based concrete (AASC). Then, the recycled tire steel fibers (RTSF) were introduced into the optimized mixture in different dosages, and the physical and mechanical properties of fiber-reinforced AASC (FR-AASC) were evaluated. RTSF inclusion negatively affected the workability and increased the density while slightly reducing the water absorption. Additionally, the compressive strength and flexural behavior of FR-AASC improved by increasing the RTSF content. The analysis of images taken from flexural specimens through the Digital Image Correlation technique (DIC) revealed that higher RTSF dosage caused a curved macro crack with several branches alongside, leading to a better post-cracking performance in terms of strength and toughness.
Optimized alkali-activated slag-based concrete reinforced with recycled tire steel fiber
This study employed Taguchi-Grey relational analysis to optimize the influences of binder content, the molarity of sodium hydroxide (SH) solution, alkaline solution to binder content (Al/Bi) ratio, water to alkali-activated solids (W/S) ratio, and sodium silicate to sodium hydroxide solution (SS/SH) ratio on the workability, setting time, and compressive strength of alkali-activated slag-based concrete (AASC). Then, the recycled tire steel fibers (RTSF) were introduced into the optimized mixture in different dosages, and the physical and mechanical properties of fiber-reinforced AASC (FR-AASC) were evaluated. RTSF inclusion negatively affected the workability and increased the density while slightly reducing the water absorption. Additionally, the compressive strength and flexural behavior of FR-AASC improved by increasing the RTSF content. The analysis of images taken from flexural specimens through the Digital Image Correlation technique (DIC) revealed that higher RTSF dosage caused a curved macro crack with several branches alongside, leading to a better post-cracking performance in terms of strength and toughness.
Optimized alkali-activated slag-based concrete reinforced with recycled tire steel fiber
Eskandarinia, Milad (Autor:in) / Esmailzade, Mina (Autor:in) / Hojatkashani, Ata (Autor:in) / Rahmani, Aida (S37579) (Autor:in) / Jahandari, Soheil (S34960) (Autor:in)
01.01.2022
Materials--1996-1944 Vol. 15 Issue. 19 No. 6623
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
DDC:
624
| TIBKAT | 2022