Corrosion rate measurements in steel sheet pile walls in a marine environment
Corrosion of steel structures in the marine environment is a major problem. The deterioration of this kind of structures is costly and difficult to predict both when designing new structures and when estimating the remaining service life time for existing structures. The aim of this investigation was to find indicative values for the corrosion rate of steel sheet piles on the Swedish west coast. Such corrosion rates (mm/year) can be used both when designing new structures by oversizing the steel thickness and when estimating the bearing capacity of existing sheet pile structures. Earlier investigations on the corrosion rates along the Swedish east coast – with salinity from about 0.2% - 0.8% – are still used today as guidelines for the corrosion rate of all steel structures in the Swedish maritime environment even though the salinity on the west coast can be as high as 3.0%. Steel sheet pile wharfs located in the port of Halmstad on the Swedish west coast were inspected by ultrasonic measurements. Three wharf structures with a total length of about 700 m were inspected. None of the inspected wharfs had or have had cathodic protection. The thickness measurements of the steel sheet pile structures were performed by divers. The age of the three inspected sheet pile structures ranged from 36 to 51 years. The dimensions of the original sheet pile sections are known. One of the quay structures is located along a river. The salinity at all wharfs varied from low values at the surface to approx. 2% at the bottom (also in the river outflow). The measured average corrosion rates were in the same order as the design values in the European code. However, the results indicate increased corrosion rates about one meter below the mean water surface and at the level of the propellers from the ships berthing the most frequented of the inspected wharfs, 3 to 6 meters below water surface. The tolerances of steel sheet thicknesses – usually in the order of ±6% – are often neglected when investigating the remaining thickness in steel ...
Corrosion rate measurements in steel sheet pile walls in a marine environment
Corrosion of steel structures in the marine environment is a major problem. The deterioration of this kind of structures is costly and difficult to predict both when designing new structures and when estimating the remaining service life time for existing structures. The aim of this investigation was to find indicative values for the corrosion rate of steel sheet piles on the Swedish west coast. Such corrosion rates (mm/year) can be used both when designing new structures by oversizing the steel thickness and when estimating the bearing capacity of existing sheet pile structures. Earlier investigations on the corrosion rates along the Swedish east coast – with salinity from about 0.2% - 0.8% – are still used today as guidelines for the corrosion rate of all steel structures in the Swedish maritime environment even though the salinity on the west coast can be as high as 3.0%. Steel sheet pile wharfs located in the port of Halmstad on the Swedish west coast were inspected by ultrasonic measurements. Three wharf structures with a total length of about 700 m were inspected. None of the inspected wharfs had or have had cathodic protection. The thickness measurements of the steel sheet pile structures were performed by divers. The age of the three inspected sheet pile structures ranged from 36 to 51 years. The dimensions of the original sheet pile sections are known. One of the quay structures is located along a river. The salinity at all wharfs varied from low values at the surface to approx. 2% at the bottom (also in the river outflow). The measured average corrosion rates were in the same order as the design values in the European code. However, the results indicate increased corrosion rates about one meter below the mean water surface and at the level of the propellers from the ships berthing the most frequented of the inspected wharfs, 3 to 6 meters below water surface. The tolerances of steel sheet thicknesses – usually in the order of ±6% – are often neglected when investigating the remaining thickness in steel ...
Corrosion rate measurements in steel sheet pile walls in a marine environment
Wall, Henrik (Autor:in) / Wadsö, Lars (Autor:in)
01.01.2013
scopus:84877901229
Marine Structures; 33, pp 21-32 (2013) ; ISSN: 1873-4170
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Corrosion rate measurements in steel sheet pile walls in a marine environment
| British Library Online Contents | 2013
Corrosion rate measurements in steel sheet pile walls in a marine environment
| Online Contents | 2013
Steel sheet pile retaining walls
| Engineering Index Backfile | 1912
| Springer Verlag | 2017