Analisis Kimia dari Serat Kayu Bangkal (Nauclea officinalis) sebagai Alternatif Bahan Baku Pulp Kertas (Chemical Analysis of Bangkal (Nauclea Officinalis) Wood Fibers as Raw Material Alternative of Pulp & Paper)
South Kalimantan has considerable natural forests and many types of timber that have not yet been optimally utilized, such as Bangkal tree (Nauclea officinalis). The purpose of this research was to analyze chemical components, dimensional fibers characteristic, and suitability of Bangkal wood as a raw material of pulp and paper. The results obtained from this study revealed that the chemical content of Bangkal wood consisted of 3.00% extractive, 30.00% lignin, 16% hemicellulose, and 50.50% cellulose. The anatomy of Bangkal wood were 1.40 mm in fiber length 1.40 mm, 1.20 μm in fiber diameter, 5.00 μm in lumen diameter, and 3.25 μm in cell wall thickness. Derived fiber values comprised Runkel Ratio (0.43), Power Weaving (66.00), Muhsteph Ratio (99.80%), Coefficient of Rigidity (0.20), and Flexibility Ratio (0.71). Based on the chemical components and quality of Bangkal wood fiber, that wood could be used as a raw material of pulp and paper.
Analisis Kimia dari Serat Kayu Bangkal (Nauclea officinalis) sebagai Alternatif Bahan Baku Pulp Kertas (Chemical Analysis of Bangkal (Nauclea Officinalis) Wood Fibers as Raw Material Alternative of Pulp & Paper)
South Kalimantan has considerable natural forests and many types of timber that have not yet been optimally utilized, such as Bangkal tree (Nauclea officinalis). The purpose of this research was to analyze chemical components, dimensional fibers characteristic, and suitability of Bangkal wood as a raw material of pulp and paper. The results obtained from this study revealed that the chemical content of Bangkal wood consisted of 3.00% extractive, 30.00% lignin, 16% hemicellulose, and 50.50% cellulose. The anatomy of Bangkal wood were 1.40 mm in fiber length 1.40 mm, 1.20 μm in fiber diameter, 5.00 μm in lumen diameter, and 3.25 μm in cell wall thickness. Derived fiber values comprised Runkel Ratio (0.43), Power Weaving (66.00), Muhsteph Ratio (99.80%), Coefficient of Rigidity (0.20), and Flexibility Ratio (0.71). Based on the chemical components and quality of Bangkal wood fiber, that wood could be used as a raw material of pulp and paper.
Analisis Kimia dari Serat Kayu Bangkal (Nauclea officinalis) sebagai Alternatif Bahan Baku Pulp Kertas (Chemical Analysis of Bangkal (Nauclea Officinalis) Wood Fibers as Raw Material Alternative of Pulp & Paper)
Herlina, Herlina (Autor:in) / Istikowati, Ph.D., Wiwin Tyas (Autor:in) / Fatriani, Fatriani (Autor:in)
28.12.2018
doi:10.24111/jrihh.v10i1.4076
Jurnal Riset Industri Hasil Hutan; Vol 10, No 1 (2018); 21-32 ; 2503-0779 ; 2086-1400
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
paper pulp , bangkal wood , fiber , chemical
DDC:
690
KOMPOSIT SERAT ALAM AKAR WANGI DAN LIMBAH SERBUK GERGAJIAN KAYU SEBAGAI BAHAN DASAR ALTERNATIF
| DOAJ | 2016
Kombinasi Campuran Limbah Moulding dan Kayu HTI untuk Pellet Kayu sebagai Bahan Bakar Alternatif
| BASE | 2016