ANALISA SIFAT KETEGUHAN PATAH DAN TEKAN BETON SEMEN DARI TULANG ROTAN
Indonesia has the potential of rattan is enough large, but the value of the sale and utilization is still limited as materials for baskets, furniture, handicrafts and so on. This research purpose to obtain bending and compressure strength properties when the rattan used for substitution of iron materaial making to cement concrete building simple houses. The raw material of used for research this is rattan has done processing (preservation and drying). Cement concrete frame made of rattan and molds for casting. Concrete frame rattan incorporated in the mold and filled dough (cement: gravel: sand = 1: 2: 3 plus water as needed). Treatment was observed that the diameter rattan (A) which includes: 8 mm (a1), 10 mm (a2) and 12 mm (a3); and the distance between the iron ring (B) which includes 11 cm (b1); 15 cm (b2); and 19 cm (b3). The number of repeat 3 times. Parameters observed bending and compressure strength.The results of the research rattan diameter 8-12 mm and the distance ring iron 11-19 cm produces bending strength from 18.24 to 40.13 kg /cm2 lower than cement concrete from iron materials (95.76 to 120.36 kg / cm2); and compressure strength from 28.33 to 42.85 kg/cm2 larger than from iron cement concrete materials (20 to 34.67kg/cm2). The results of the research show bending strength from rattan lower and compressure sterngth than big concrete from iron.Keywords: rattan, cement concrete, bending strength, compressure strength
ANALISA SIFAT KETEGUHAN PATAH DAN TEKAN BETON SEMEN DARI TULANG ROTAN
Indonesia has the potential of rattan is enough large, but the value of the sale and utilization is still limited as materials for baskets, furniture, handicrafts and so on. This research purpose to obtain bending and compressure strength properties when the rattan used for substitution of iron materaial making to cement concrete building simple houses. The raw material of used for research this is rattan has done processing (preservation and drying). Cement concrete frame made of rattan and molds for casting. Concrete frame rattan incorporated in the mold and filled dough (cement: gravel: sand = 1: 2: 3 plus water as needed). Treatment was observed that the diameter rattan (A) which includes: 8 mm (a1), 10 mm (a2) and 12 mm (a3); and the distance between the iron ring (B) which includes 11 cm (b1); 15 cm (b2); and 19 cm (b3). The number of repeat 3 times. Parameters observed bending and compressure strength.The results of the research rattan diameter 8-12 mm and the distance ring iron 11-19 cm produces bending strength from 18.24 to 40.13 kg /cm2 lower than cement concrete from iron materials (95.76 to 120.36 kg / cm2); and compressure strength from 28.33 to 42.85 kg/cm2 larger than from iron cement concrete materials (20 to 34.67kg/cm2). The results of the research show bending strength from rattan lower and compressure sterngth than big concrete from iron.Keywords: rattan, cement concrete, bending strength, compressure strength
ANALISA SIFAT KETEGUHAN PATAH DAN TEKAN BETON SEMEN DARI TULANG ROTAN
Purwanto, Djoko (Autor:in)
31.12.2014
doi:10.24111/jrihh.v6i2.1232
Jurnal Riset Industri Hasil Hutan; Vol 6, No 2 (2014); 7-12 ; 2503-0779 ; 2086-1400
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
DDC:
690
Pengaruh Penambahan Admixture Terhadap Kuat Tekan Beton Dari Berbagai Merek Semen
| BASE | 2020
ANALISA PERBANDINGAN PENAMBAHAN VARIASI CONSOL TERHADAP KUAT TEKAN BETON
| DOAJ | 2018