Effect of Water-Cement Ratio on Flexural Strength of RC Beams Made with Partial Replacement of Coarse Aggregates with Coarse Aggregates from Old Concrete
This research paper presents an experimental evaluation of the effect of water-cement ratio on the flexural strength of reinforced concrete beams made with 50% replacement of coarse aggregates with recycled concrete aggregates (RCA). 72 reinforced concrete beams were cast using 0.54, 0.6, 0.65 and 0.70 water-cement ratio. In each ratio, 12 beams were cast using RCA and 3 beams were cast using all-natural coarse aggregates (NCA). Beams were cured for 7 and 28 days. After curing, all beams were tested with central point load in a universal load testing machine. From the obtained results, it is observed that the maximum reduction in flexural strength of RCA beams is about 28% when compared to the 0.54 w/c ratio beams of the same group and 31.75% in comparison to NCA beams cast with same w/c ratio. The maximum deflection and average strain in beams remained within limits. The observed cracking pattern shows shear failure of all beams.
Effect of Water-Cement Ratio on Flexural Strength of RC Beams Made with Partial Replacement of Coarse Aggregates with Coarse Aggregates from Old Concrete
This research paper presents an experimental evaluation of the effect of water-cement ratio on the flexural strength of reinforced concrete beams made with 50% replacement of coarse aggregates with recycled concrete aggregates (RCA). 72 reinforced concrete beams were cast using 0.54, 0.6, 0.65 and 0.70 water-cement ratio. In each ratio, 12 beams were cast using RCA and 3 beams were cast using all-natural coarse aggregates (NCA). Beams were cured for 7 and 28 days. After curing, all beams were tested with central point load in a universal load testing machine. From the obtained results, it is observed that the maximum reduction in flexural strength of RCA beams is about 28% when compared to the 0.54 w/c ratio beams of the same group and 31.75% in comparison to NCA beams cast with same w/c ratio. The maximum deflection and average strain in beams remained within limits. The observed cracking pattern shows shear failure of all beams.
Effect of Water-Cement Ratio on Flexural Strength of RC Beams Made with Partial Replacement of Coarse Aggregates with Coarse Aggregates from Old Concrete
Oad, Mahboob (Autor:in) / Buller, Abdul Hafeez (Autor:in) / Memon, Bashir Ahmed (Autor:in) / Memon, Noor Ahmed (Autor:in) / Tunio, Zaheer Ahmed (Autor:in) / Memon, Muneeb Ayoob (Autor:in)
16.02.2019
oai:zenodo.org:2576355
Engineering, Technology & Applied Science Research 9(1) 3826-3831
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
DDC:
690
Partial Replacement of Fine Aggregates, Coarse Aggregates, Cement in Concrete
BASE | 2021
|Springer Verlag | 2022
|