Factors influencing thermal conductivity and compressive strength of natural fiber-reinforced geopolymer foams
New sustainable, environmentally friendly materials for thermal insulation of buildings are necessary to reduce their carbon footprints. In this study, Miscanthus fiber-reinforced geopolymer composites, foamed with sodium dodecyl sulfate (SDS), were developed using fly ash as a geopolymer precursor. The effects of fiber content, fiber size, curing temperature, foaming agent content, fumed silica specific surface area and fumed silica content on thermal conductivity and compressive strength were evaluated using a Plackett-Burman design of experiment. Furthermore, the microstructure of geopolymer composites was investigated using X-ray diffraction (XRD), X-ray micro-computed tomography (μCT) and scanning electron microscopy (SEM). The measured characteristic values were in the following ranges: Thermal conductivity 0.057 W (m K)−1 to 0.127 W (m K)−1, compressive strength 0.007 MPa–0.719 MPa and porosity 49 vol% to 76 vol%. The results reveal an enhancement of thermal conductivity by elevated fiber size and foaming agent content. In contrast, the compressive strength is enhanced by high fiber content. Additionally, SEM images indicate a good interaction between the fibers and the geopolymer matrix, because nearly the whole fiber surface is covered by the geopolymer.
Factors influencing thermal conductivity and compressive strength of natural fiber-reinforced geopolymer foams
New sustainable, environmentally friendly materials for thermal insulation of buildings are necessary to reduce their carbon footprints. In this study, Miscanthus fiber-reinforced geopolymer composites, foamed with sodium dodecyl sulfate (SDS), were developed using fly ash as a geopolymer precursor. The effects of fiber content, fiber size, curing temperature, foaming agent content, fumed silica specific surface area and fumed silica content on thermal conductivity and compressive strength were evaluated using a Plackett-Burman design of experiment. Furthermore, the microstructure of geopolymer composites was investigated using X-ray diffraction (XRD), X-ray micro-computed tomography (μCT) and scanning electron microscopy (SEM). The measured characteristic values were in the following ranges: Thermal conductivity 0.057 W (m K)−1 to 0.127 W (m K)−1, compressive strength 0.007 MPa–0.719 MPa and porosity 49 vol% to 76 vol%. The results reveal an enhancement of thermal conductivity by elevated fiber size and foaming agent content. In contrast, the compressive strength is enhanced by high fiber content. Additionally, SEM images indicate a good interaction between the fibers and the geopolymer matrix, because nearly the whole fiber surface is covered by the geopolymer.
Factors influencing thermal conductivity and compressive strength of natural fiber-reinforced geopolymer foams
Walbrück, Katharina (Autor:in) / Drewler, Lisabeth (Autor:in) / Witzleben, Steffen (Autor:in) / Stephan, Dietmar (Autor:in)
31.01.2021
Open Ceramics ; ISSN 2666-5395 ; Open Ceramics 5 (2021) 100065
Aufsatz (Zeitschrift)