Sifat Fisis Dan Keunggulan Papan Semen Dari Limbah Kulit Batang Sagu
This research aimed to determine the physical properties and advantages of cement boards made from sago stem bark waste based on the test results of several parameters according to JIS A 5908 (2003) standard. The results showed that the physical properties of cement board from sago stem bark waste with the addition of the CaCl2 catalyst were good, with the average value of density ranged from 1.19-1.26 gr/cm³, water content 7,67-8,02%, and water absorption after immersion 2 hours 6,03-7.65% as well as after 24-hour immersion 11,62-12,91%, respectively. The averages swelling value of board thickness was 1.62-12,91% after immersion 2 hours and 1.40-3.41% after immersion 24 hours. Furthermore, what sago bark waste in various positions of the tree trunk (tree base, middle and top) can be utilized to manufacture cement board. The board made from sago stem bark waste at the base position with a catalyst CaCl2 6% has the best physical properties and meets JIS A 5908 (2003) standard. Cement board from sago stem bark waste has an excellent waterproof capability and can be used as outdoor materials.
Sifat Fisis Dan Keunggulan Papan Semen Dari Limbah Kulit Batang Sagu
This research aimed to determine the physical properties and advantages of cement boards made from sago stem bark waste based on the test results of several parameters according to JIS A 5908 (2003) standard. The results showed that the physical properties of cement board from sago stem bark waste with the addition of the CaCl2 catalyst were good, with the average value of density ranged from 1.19-1.26 gr/cm³, water content 7,67-8,02%, and water absorption after immersion 2 hours 6,03-7.65% as well as after 24-hour immersion 11,62-12,91%, respectively. The averages swelling value of board thickness was 1.62-12,91% after immersion 2 hours and 1.40-3.41% after immersion 24 hours. Furthermore, what sago bark waste in various positions of the tree trunk (tree base, middle and top) can be utilized to manufacture cement board. The board made from sago stem bark waste at the base position with a catalyst CaCl2 6% has the best physical properties and meets JIS A 5908 (2003) standard. Cement board from sago stem bark waste has an excellent waterproof capability and can be used as outdoor materials.
Sifat Fisis Dan Keunggulan Papan Semen Dari Limbah Kulit Batang Sagu
Maail, Rohny S. (Autor:in) / Derlauw, Irfan (Autor:in)
30.12.2020
doi:10.30598/makila.v14i2.2895
MAKILA: Jurnal Penelitian Kehutanan; Vol 14 No 2 (2020): Makila : Jurnal Penelitian Kehutanan; 87-98 ; 2746-7155 ; 1978-4996 ; 10.30598/makila.v14i2
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
DDC:
710
SIFAT FISIKA DAN MEKANIKA PAPAN SEMEN DARI SERAT KULIT BATANG SAGU (Metroxylon Sp)
| BASE | 2019