STUDY KEGAGALAN AKIBAT KOROSI PADA PIPA ECONOMIZER
Failure analysis to the economizer tube of boiler with operation pressure ± 190 bar, in holding time 6 hour have been investigated. The economizer tube is carbon steel, ASTM A210 Grade C, outside diameter ± 51 mm and thickness ± 6 mm. The investigation cause of failure from the economizer tube included : chemical composition and metallography analysis, visual examination at outer and inner fire side, measuring thickness and densities of the scale at inner fire side and wall side, chemical composition analysis of the at surface crust the economizer tube. From the results of visual investigation to both outer and inner fire side of the economizer tube shown that at fire side occur decrease thickness of the wall tube, with minimum thickness are 1.37 mm and 2,50 mm, respectively. Those caused by erosion corrosion result from effect the fly ash. Beside that, at inner fire side of the economizer tube occur light pitting corrosion result by oxygen corrosion.Keywords : Economizer tube, boiler, fire side, fly ash, erosion corrosion, pitting corrosion, scale, oxygen
STUDY KEGAGALAN AKIBAT KOROSI PADA PIPA ECONOMIZER
Failure analysis to the economizer tube of boiler with operation pressure ± 190 bar, in holding time 6 hour have been investigated. The economizer tube is carbon steel, ASTM A210 Grade C, outside diameter ± 51 mm and thickness ± 6 mm. The investigation cause of failure from the economizer tube included : chemical composition and metallography analysis, visual examination at outer and inner fire side, measuring thickness and densities of the scale at inner fire side and wall side, chemical composition analysis of the at surface crust the economizer tube. From the results of visual investigation to both outer and inner fire side of the economizer tube shown that at fire side occur decrease thickness of the wall tube, with minimum thickness are 1.37 mm and 2,50 mm, respectively. Those caused by erosion corrosion result from effect the fly ash. Beside that, at inner fire side of the economizer tube occur light pitting corrosion result by oxygen corrosion.Keywords : Economizer tube, boiler, fire side, fly ash, erosion corrosion, pitting corrosion, scale, oxygen
STUDY KEGAGALAN AKIBAT KOROSI PADA PIPA ECONOMIZER
Wagiman, Acep (Autor:in) / Gundara, Gugun (Autor:in)
31.12.2017
doi:10.24127/trb.v6i2.625
Turbo : Jurnal Program Studi Teknik Mesin; Vol 6, No 2 (2017): Desember 2017 ; TURBO [Tulisan Riset Berbasis Online]; Vol 6, No 2 (2017): Desember 2017 ; 2477-250X ; 2301-6663
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
DDC:
690
Pengaruh Korosi Terhadap Kegagalan Logam pada Jembatan : Literature Review
| DOAJ | 2022
| DOAJ | 2015
ANALISIS KEBOCORAN BELOKAN PIPA EVAPORATOR PADA HRSG AKIBAT BEBAN TERMAL
| DOAJ | 2018
Simulasi Numerik berbasi Komputer sebagai Solusi Pencegah Bahaya Akibat Kegagalan Bangunan
| DOAJ | 2019