The Influence of Mineraliser Granulometry on Dense Silica Brick Microstructure
This entry concerned with dense silica bricks microstructure was produced as a part of a project within the Technology Agency of the Czech Republic which is being implemented in cooperation of the biggest producer of refractories the P-D Refractories CZ company with the research organisation Brno University of Technology. The paper is focused on the influence of mixture homogenisation and the influence of grain size of the mineraliser on the resulting utility properties of the material as well as its microstructure. It has a decisive influence on the durability of the material in a building structure. This paper is a continuation of a previously published study dealing with the suitability of various types of mineralising agents in terms of density, strength and mineral composition of silica brick. The entry describes the influence of the method of mixture homogenisation and the influence of granulometry of the applied Femineralising agent on the resulting silica microstructure. Porosity, density, phase composition and microstructure of the experimentally prepared silica bricks samples were examined and the results were discussed in context with the technology of homogenisation and firing temperature used. The properties of silica bricks samples were compared to the sample without any Fe-mineraliser.
The Influence of Mineraliser Granulometry on Dense Silica Brick Microstructure
This entry concerned with dense silica bricks microstructure was produced as a part of a project within the Technology Agency of the Czech Republic which is being implemented in cooperation of the biggest producer of refractories the P-D Refractories CZ company with the research organisation Brno University of Technology. The paper is focused on the influence of mixture homogenisation and the influence of grain size of the mineraliser on the resulting utility properties of the material as well as its microstructure. It has a decisive influence on the durability of the material in a building structure. This paper is a continuation of a previously published study dealing with the suitability of various types of mineralising agents in terms of density, strength and mineral composition of silica brick. The entry describes the influence of the method of mixture homogenisation and the influence of granulometry of the applied Femineralising agent on the resulting silica microstructure. Porosity, density, phase composition and microstructure of the experimentally prepared silica bricks samples were examined and the results were discussed in context with the technology of homogenisation and firing temperature used. The properties of silica bricks samples were compared to the sample without any Fe-mineraliser.
The Influence of Mineraliser Granulometry on Dense Silica Brick Microstructure
L. Nevrivova (Autor:in) / K. Lang (Autor:in) / M. Kotoucek (Autor:in) / D. Vsiansky (Autor:in)
02.10.2014
oai:zenodo.org:1096715
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
DDC:
690
The Influence of Mineraliser Granulometry on Dense Silica Brick Microstructure
| BASE | 2014
Visual Granulometry: Image-based Granulometry of Concrete Aggregate
| DataCite | 2022
| Wiley | 2012
| DataCite | 2022
Influence of Different Grinding Types on Granulometry of Cement Grains
| British Library Conference Proceedings | 2014