Fire Spalling of Concrete : Theoretical and Experimental Studies
Fire spalling of concrete is not a new phenomenon. To some degree there has always been a risk during rapid heating of concrete. Therefore, to a certain degree the effect of fire spalling is included in the bank of data from fire tests and fires on which our understanding of the fire resistance of concrete is based. However, the development and modern use of more dense concrete mixes have produced cases of very severe fire spalling which have increased the urgency to understand this phenomenon. In this context, the use of an addition of polypropylene (PP) fibres to the mix to limit the amount of spalling has been one topic of interest for this thesis. During fire tests on a post-tensioned concrete structure made of spalling sensitive concrete, it has been shown that substantially lower amounts of PP fibres than 2 kg/m3, which is recommended in the Eurocode (1992-1-2:2004), can be used with successful results. As part of this study, another important aspect has emerged, i.e. the impact the test method used can have on the fire spalling depths observed in concrete specimens. This has been known for many years but is seldom discussed in the scientific literature. In this thesis it has been shown that results from tests on unloaded cubes do not necessarily correspond to results seen on larger loaded slabs. In the results presented, none of the tested cubes spalled whereas some of the large slabs spalled to the degree that the reinforcement became fire exposed. Further, the difference in spalling depths between small and large post-tensioned slabs was shown to be substantial; although in general the ranking in severity from least to greatest spalling correlated between these two specimen sizes. The correlation to larger specimens was much vaguer in the case when the small slabs were not loaded in compression as there sometimes was no spalling in the small slabs. From time to time the randomness of the fire spalling of concrete has been mentioned. To investigate this further, an analysis of 110 fire tests performed on ...
Fire Spalling of Concrete : Theoretical and Experimental Studies
Fire spalling of concrete is not a new phenomenon. To some degree there has always been a risk during rapid heating of concrete. Therefore, to a certain degree the effect of fire spalling is included in the bank of data from fire tests and fires on which our understanding of the fire resistance of concrete is based. However, the development and modern use of more dense concrete mixes have produced cases of very severe fire spalling which have increased the urgency to understand this phenomenon. In this context, the use of an addition of polypropylene (PP) fibres to the mix to limit the amount of spalling has been one topic of interest for this thesis. During fire tests on a post-tensioned concrete structure made of spalling sensitive concrete, it has been shown that substantially lower amounts of PP fibres than 2 kg/m3, which is recommended in the Eurocode (1992-1-2:2004), can be used with successful results. As part of this study, another important aspect has emerged, i.e. the impact the test method used can have on the fire spalling depths observed in concrete specimens. This has been known for many years but is seldom discussed in the scientific literature. In this thesis it has been shown that results from tests on unloaded cubes do not necessarily correspond to results seen on larger loaded slabs. In the results presented, none of the tested cubes spalled whereas some of the large slabs spalled to the degree that the reinforcement became fire exposed. Further, the difference in spalling depths between small and large post-tensioned slabs was shown to be substantial; although in general the ranking in severity from least to greatest spalling correlated between these two specimen sizes. The correlation to larger specimens was much vaguer in the case when the small slabs were not loaded in compression as there sometimes was no spalling in the small slabs. From time to time the randomness of the fire spalling of concrete has been mentioned. To investigate this further, an analysis of 110 fire tests performed on ...
Fire Spalling of Concrete : Theoretical and Experimental Studies
Jansson, Robert (Autor:in)
01.01.2013
117
Hochschulschrift
Elektronische Ressource
Englisch
Experimental analysis of concrete spalling due to fire exposure
| Taylor & Francis Verlag | 2013
An experimental fire-spalling assessment procedure for concrete mixtures
| Elsevier | 2019
Explosive spalling of concrete in fire
| TIBKAT | 2014
Explosive spalling of concrete in fire
| UB Braunschweig | 2014