Effect of Temperature and Humidity on the Synthesis of Alkali-Activated Binders Based on Bottom Ash from Municipal Waste Incineration
Weathered bottom ash (WBA) from municipal solid waste incineration is a calcium aluminosilicate-rich material mainly used in construction and civil engineering as a secondary aggregate. However, its use is also being considered as a precursor in the manufacture of alkali-activated binders (AA-WBA). This preliminary research aimed to deepen understanding of the potential use of WBA (>8 mm fraction) as the sole precursor of alkali-activated binders. To gain better knowledge of this material, the physicochemical, mechanical, and environmental properties of AA-WBA binders were evaluated. In addition, the effect of curing temperature (25 °C, 45 °C, 65 °C, and 85 °C) and humidity conditions (oven and climate chamber) were assessed. The results of this study revealed that temperature and humidity conditions play a fundamental role during the early formation stages of AA-WBA binders. Maximum compactness and compressive strength (29.8 MPa) were obtained in the sample cured at 65 °C in the oven and room humidity. At higher temperatures (85 °C), a substantial decrease in mechanical strength (21.2 MPa) was observed due to a lower cohesion of the binder phases. Curing in the climate chamber led to an increase in humidity, and therefore a decrease in compressive strength. Finally, lower porosity and longer curing time substantially decreased the heavy metals and metalloid leaching concentration of AA-WBA binders.
Effect of Temperature and Humidity on the Synthesis of Alkali-Activated Binders Based on Bottom Ash from Municipal Waste Incineration
Weathered bottom ash (WBA) from municipal solid waste incineration is a calcium aluminosilicate-rich material mainly used in construction and civil engineering as a secondary aggregate. However, its use is also being considered as a precursor in the manufacture of alkali-activated binders (AA-WBA). This preliminary research aimed to deepen understanding of the potential use of WBA (>8 mm fraction) as the sole precursor of alkali-activated binders. To gain better knowledge of this material, the physicochemical, mechanical, and environmental properties of AA-WBA binders were evaluated. In addition, the effect of curing temperature (25 °C, 45 °C, 65 °C, and 85 °C) and humidity conditions (oven and climate chamber) were assessed. The results of this study revealed that temperature and humidity conditions play a fundamental role during the early formation stages of AA-WBA binders. Maximum compactness and compressive strength (29.8 MPa) were obtained in the sample cured at 65 °C in the oven and room humidity. At higher temperatures (85 °C), a substantial decrease in mechanical strength (21.2 MPa) was observed due to a lower cohesion of the binder phases. Curing in the climate chamber led to an increase in humidity, and therefore a decrease in compressive strength. Finally, lower porosity and longer curing time substantially decreased the heavy metals and metalloid leaching concentration of AA-WBA binders.
Effect of Temperature and Humidity on the Synthesis of Alkali-Activated Binders Based on Bottom Ash from Municipal Waste Incineration
Tortora, Pietro C.D. (Autor:in) / Maldonado Alameda, Alex (Autor:in) / Mañosa Bover, Jofre (Autor:in) / Quintero-Payan, Alex C. (Autor:in) / Leonelli, Cristina (Autor:in) / Lancellotti, I. (Autor:in) / Chimenos Ribera, Josep Ma. (Autor:in)
06.02.2022
718282
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
DDC:
690
Alkali-activated binders based on municipal solid waste incineration bottom ash
| BASE | 2021
| BASE | 2020
Mechanical properties of incineration bottom ash from municipal waste
| British Library Conference Proceedings | 2008
High-Volume Municipal Solid Waste Incineration Bottom Ash Concrete
| British Library Conference Proceedings | 2017