Effect of helium irradiation on the hydrogen isotope retention in tungsten by in situ TEM and STEM-EELS analysis
The microscopic effects of He irradiation on the H isotope retention in W were quantitatively evaluated using two types of high-function transmission electron microscopes: an ion-gun directly coupled TEM equipped with a high-resolution quadrupole mass spectrometer and an aberration-corrected scanning TEM combined with electron energy-loss spectrometer (STEM-EELS). He pre-irradiation induced fine and dense bubbles near the surface of the samples, thereby significantly increasing the deuterium (D) retention. The STEM-EELS analysis revealed that most of the D atoms were trapped and distributed homogeneously in the bubbles and released at relatively low temperatures without microstructural changes with increasing temperature. In contrast, some of the He was dissociated from the bubble by D post-irradiation in the matrix with a metastable state and retrapped by the bubble as the temperature was increased.
Effect of helium irradiation on the hydrogen isotope retention in tungsten by in situ TEM and STEM-EELS analysis
The microscopic effects of He irradiation on the H isotope retention in W were quantitatively evaluated using two types of high-function transmission electron microscopes: an ion-gun directly coupled TEM equipped with a high-resolution quadrupole mass spectrometer and an aberration-corrected scanning TEM combined with electron energy-loss spectrometer (STEM-EELS). He pre-irradiation induced fine and dense bubbles near the surface of the samples, thereby significantly increasing the deuterium (D) retention. The STEM-EELS analysis revealed that most of the D atoms were trapped and distributed homogeneously in the bubbles and released at relatively low temperatures without microstructural changes with increasing temperature. In contrast, some of the He was dissociated from the bubble by D post-irradiation in the matrix with a metastable state and retrapped by the bubble as the temperature was increased.
Effect of helium irradiation on the hydrogen isotope retention in tungsten by in situ TEM and STEM-EELS analysis
Mitsutaka Miyamoto (Autor:in) / Kohei Sano (Autor:in) / Tomoya Sawae (Autor:in) / Mitsutaka Haruta (Autor:in) / Hiroki Kurata (Autor:in)
2023
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Tungsten evolution under helium irradiation: Shape of bubbles by TEM and in-situ GISAXS analysis
| DOAJ | 2023
Irradiation effects of hydrogen and helium plasma on different grade tungsten materials
| DOAJ | 2017
| DOAJ | 2022
Tungsten evolution under helium irradiation: Shape of bubbles by TEM and in-situ GISAXS analysis
| Elsevier | 2023