This study analyzes bricks manufactured from bagasse, a by-product of the brewing industry. Raw materials (clay and bagasse) were characterized to determine their chemical composition, mineralogical composition and thermal behaviour. Mixtures were prepared with amounts of 0, 2.5, 5, 7.5 and 10 wt% of bagasse incorporated into the clay body. Rectangular test pieces were obtained by application of 54.5 MPa pressure, they were dried at 110 °C and fired at 950 ºC in a laboratory furnace for 1 hour. Ceramic properties related to weight loss on ignition, linear shrinkage, bulk and absolute density, water absorption, water suction and compressive strength were analyzed in order to evaluate the suitability of using this wastes in ceramic matrix to the production of building bricks. The results indicate that the incorporation of the bagasse decreases the absolute and bulk density, increases the water absorption and reduces the compressive strength of the brick.
Utilization of bagasse from the beer industry in clay brick production for building
This study analyzes bricks manufactured from bagasse, a by-product of the brewing industry. Raw materials (clay and bagasse) were characterized to determine their chemical composition, mineralogical composition and thermal behaviour. Mixtures were prepared with amounts of 0, 2.5, 5, 7.5 and 10 wt% of bagasse incorporated into the clay body. Rectangular test pieces were obtained by application of 54.5 MPa pressure, they were dried at 110 °C and fired at 950 ºC in a laboratory furnace for 1 hour. Ceramic properties related to weight loss on ignition, linear shrinkage, bulk and absolute density, water absorption, water suction and compressive strength were analyzed in order to evaluate the suitability of using this wastes in ceramic matrix to the production of building bricks. The results indicate that the incorporation of the bagasse decreases the absolute and bulk density, increases the water absorption and reduces the compressive strength of the brick.
Utilization of bagasse from the beer industry in clay brick production for building
M. L. Martínez (Autor:in) / D. Eliche (Autor:in) / N. Cruz (Autor:in) / F. A. Corpas (Autor:in)
2012
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Utilization of kraft pulp production residues in clay brick production
| Online Contents | 2005
Utilization of kraft pulp production residues in clay brick production
| British Library Online Contents | 2005
The Utilization of Brick and Clay Products in Nigerian Construction Industry
| British Library Conference Proceedings | 1985
Utilization of Palm Oil Fuel Ash in Brick Manufacturing for Lightweight Fired Clay Brick Production
| BASE | 2020
Brick and clay building in Britain
| UB Braunschweig | 2008