Flexural Fatigue Behaviors of Silicon Carbide Recycled Concrete in Corrosive Environments
An experimental study on the flexural fatigue behaviors of recycled concrete (RC) and silicon carbide recycled concrete (SiCRC) was conducted. The immersion time was 0 d, 30 d, 60 d, and 90 d in 5% NaCl solution for these two kinds of recycled concrete specimens, respectively, and then, four-point flexural fatigue tests were performed by MTS fatigue testing machine. The fatigue life for varying stress levels ranging from 0.9 to 0.6 was obtained. The fatigue life was given considering the failure probability according to the fatigue life and stress level of the specimen via the logarithmic normal distribution and Weibull distribution, respectively. The relationship between fatigue life and failure probability was also obtained. The fatigue life with failure probability of 1% and 50% was further predicted. The results showed that the fatigue life of RC and SiCRC increased in corrosive environments. The fatigue life of SiCRC is higher than that of RC, and the incorporation of SiCRC can improve the fatigue life of recycled concrete.
Flexural Fatigue Behaviors of Silicon Carbide Recycled Concrete in Corrosive Environments
An experimental study on the flexural fatigue behaviors of recycled concrete (RC) and silicon carbide recycled concrete (SiCRC) was conducted. The immersion time was 0 d, 30 d, 60 d, and 90 d in 5% NaCl solution for these two kinds of recycled concrete specimens, respectively, and then, four-point flexural fatigue tests were performed by MTS fatigue testing machine. The fatigue life for varying stress levels ranging from 0.9 to 0.6 was obtained. The fatigue life was given considering the failure probability according to the fatigue life and stress level of the specimen via the logarithmic normal distribution and Weibull distribution, respectively. The relationship between fatigue life and failure probability was also obtained. The fatigue life with failure probability of 1% and 50% was further predicted. The results showed that the fatigue life of RC and SiCRC increased in corrosive environments. The fatigue life of SiCRC is higher than that of RC, and the incorporation of SiCRC can improve the fatigue life of recycled concrete.
Flexural Fatigue Behaviors of Silicon Carbide Recycled Concrete in Corrosive Environments
Jinzhi Zhou (Autor:in) / Tiantian Fu (Autor:in) / Chuheng Zhong (Autor:in) / Kun Peng (Autor:in) / Ziyang Shuang (Autor:in)
2021
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Fracture and flexural behaviors of recycled lump-aggregate concrete
| Elsevier | 2023
| British Library Online Contents | 2014
Flexural Behaviors of Modified Recycled Aggregate Concrete Reinforced with Pultruded GFRP
| Trans Tech Publications | 2022