Carbonation of calcium aluminate cement pastes
This work discusses the results from accelerated tests intended to investigate the ways the different curing methods affect the carbonation of calcium aluminate cements pastes (CAC). The research was focused on the mineralogical composition of hydrated and carbonated samples. The compressive strengths and the porosity of the samples have been determined. Results point out that vaterite and aragonite are formed as a result of carbonation of both cubic and hexagonal calcium aluminate hydrates. The polymorph of calcium carbonate formed does not depend on the curing process. Carbonation rates is higher in hexagonal than in cubic hydrates. Results obtained through this study evidence that, as a consequence of the carbonation process of CAC pastes, in test conditions, an increase of the mechanical strengths occurs.
Carbonation of calcium aluminate cement pastes
This work discusses the results from accelerated tests intended to investigate the ways the different curing methods affect the carbonation of calcium aluminate cements pastes (CAC). The research was focused on the mineralogical composition of hydrated and carbonated samples. The compressive strengths and the porosity of the samples have been determined. Results point out that vaterite and aragonite are formed as a result of carbonation of both cubic and hexagonal calcium aluminate hydrates. The polymorph of calcium carbonate formed does not depend on the curing process. Carbonation rates is higher in hexagonal than in cubic hydrates. Results obtained through this study evidence that, as a consequence of the carbonation process of CAC pastes, in test conditions, an increase of the mechanical strengths occurs.
Carbonation of calcium aluminate cement pastes
L. Fernández-Carrasco (Autor:in) / F. Puertas (Autor:in) / M. T. Blanco-Varela (Autor:in) / T. Vázquez (Autor:in)
2001
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Supercritical carbonation of calcium aluminate cement
| Online Contents | 2008
Supercritical carbonation of calcium aluminate cement
| Elsevier | 2008
Supercritical carbonation of calcium aluminate cement
| Online Contents | 2008
Supercritical carbonation of calcium aluminate cement
| British Library Online Contents | 2008
Accelerated carbonation of calcium aluminate cement paste
| Tema Archiv | 2001