RESEARCH ON PROPAGATION CHARACTERISTICS OF FATIGUE CRACK AND LIFE PREDICTION FOR THE PANTOGRAPH
The three-dimensional finite element model of the pantograph was established by the finite element software,and the propagation characteristics of fatigue crack at the end of the upper frame for the pantograph were studied by the fracture analysis software Franc3 D. The fatigue crack propagation life under normal temperature,atmospheric environment and corrosion environment were predicted. The results show that when a 2 mm surface crack has been produced at the end of pantograph upper frame,it will penetrate the pipe wall when it continues to expand to a surface length of about 15 mm. For normal temperature and atmospheric environment,the operation mileage of fatigue crack extension from 2 mm surface crack to 50 mm through crack is about 240 000 km. In the corrosive environment,the operation mileage of surface cracks extension to the same length is about31 900 km.
RESEARCH ON PROPAGATION CHARACTERISTICS OF FATIGUE CRACK AND LIFE PREDICTION FOR THE PANTOGRAPH
The three-dimensional finite element model of the pantograph was established by the finite element software,and the propagation characteristics of fatigue crack at the end of the upper frame for the pantograph were studied by the fracture analysis software Franc3 D. The fatigue crack propagation life under normal temperature,atmospheric environment and corrosion environment were predicted. The results show that when a 2 mm surface crack has been produced at the end of pantograph upper frame,it will penetrate the pipe wall when it continues to expand to a surface length of about 15 mm. For normal temperature and atmospheric environment,the operation mileage of fatigue crack extension from 2 mm surface crack to 50 mm through crack is about 240 000 km. In the corrosive environment,the operation mileage of surface cracks extension to the same length is about31 900 km.
RESEARCH ON PROPAGATION CHARACTERISTICS OF FATIGUE CRACK AND LIFE PREDICTION FOR THE PANTOGRAPH
JING SuoLi (Autor:in) / JIA BuChao (Autor:in) / YU YanZun (Autor:in) / ZHOU Ning (Autor:in) / LI Jing (Autor:in) / LIU JiuRui (Autor:in) / CHENG Yao (Autor:in)
2021
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
RESEARCH ON FATIGUE CRACK PROPAGATION BEHAVIOR AND LIFE PREDICTION OF WIND TURBINE GEAR
| DOAJ | 2022
Fatigue life prediction based on crack propagation and acoustic emission count rates
| Online Contents | 2003
| British Library Online Contents | 2008