Colour and Chemical Changes of Black Locust Wood during Heat Treatment
Black locust is a fast-growing deciduous tree species with multiple industrial purposes due to its valuable traits. However, the heterogeneity of colour distribution between sapwood and heartwood limits its application. Thermal modification is an environment-friendly technology for improving various wood properties, especially dimensional stability, decay resistance, and colour homogeneity. In this work, black locust (Robinia pseudoacacia L.) wood samples were thermally modified at temperatures of 160, 180, and 210 °C. Extractives and main wood components were analysed by wet chemical methods, colour was measured by spectrometry, and structural changes by Fourier transform infrared spectroscopy. The obtained results show that the darkening of black locust wood, unlike other wood species of the temperate zone, is mainly caused by changes in extractives. Their content decreases during thermal treatment, but new chromophores are formed, especially in quinones. Degradation of hemicelluloses and the partial degradation of cellulose also contribute to colour changes. At higher temperatures, condensation reactions can occur in lignin, leading to the formation of some chromophores. Statistical analysis confirmed that temperature can be considered a very significant factor affecting the colour of the wood surface.
Colour and Chemical Changes of Black Locust Wood during Heat Treatment
Black locust is a fast-growing deciduous tree species with multiple industrial purposes due to its valuable traits. However, the heterogeneity of colour distribution between sapwood and heartwood limits its application. Thermal modification is an environment-friendly technology for improving various wood properties, especially dimensional stability, decay resistance, and colour homogeneity. In this work, black locust (Robinia pseudoacacia L.) wood samples were thermally modified at temperatures of 160, 180, and 210 °C. Extractives and main wood components were analysed by wet chemical methods, colour was measured by spectrometry, and structural changes by Fourier transform infrared spectroscopy. The obtained results show that the darkening of black locust wood, unlike other wood species of the temperate zone, is mainly caused by changes in extractives. Their content decreases during thermal treatment, but new chromophores are formed, especially in quinones. Degradation of hemicelluloses and the partial degradation of cellulose also contribute to colour changes. At higher temperatures, condensation reactions can occur in lignin, leading to the formation of some chromophores. Statistical analysis confirmed that temperature can be considered a very significant factor affecting the colour of the wood surface.
Colour and Chemical Changes of Black Locust Wood during Heat Treatment
František Kačík (Autor:in) / Ivan Kubovský (Autor:in) / Jiří Bouček (Autor:in) / Richard Hrčka (Autor:in) / Milan Gaff (Autor:in) / Danica Kačíková (Autor:in)
2022
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Colour responses of black locust (Robinia pseudoacacia L.) to solvent extraction and heat treatment
| British Library Online Contents | 2010
| British Library Online Contents | 2003
Heat treatment of solid wood : effects on absorption, strength and colour
| BASE | 2008
Colour and chemical changes on photodegraded beech wood with or without red heartwood
| British Library Online Contents | 2014