TiO2-WO3 Loaded onto Wood Surface for Photocatalytic Degradation of Formaldehyde
In this work, a facile method was adopted to prepare TiO2-WO3 loaded onto a wood surface by a two-step hydrothermal method. The as-prepared wood composite material can be used as a photocatalyst under UV irradiation for the photodegradation of formaldehyde. Related tests showed that TiO2-WO3 nano-architectonic materials with spherical particles loaded onto the wood substratewere mainly caused by self-photodegradation of formaldehyde. The TiO2-WO3 nanostructured material firmly adheres to the wood substrate through electrostatic and hydrogen bonding interactions. Meanwhile, the appearance of the new chemical bond Ti-O-W indicates the successful loading of TiO2-WO3 onto the wood surface. The photodegradation rate was measured and it was confirmed that the highest photodegradation performance of the modified wood was achieved at a molar ratio of 5:1 of TiO2 to WO3. This work provides a new strategy for the preparing of novel photocatalysts based on wood substrate. Moreover, the wood loaded with TiO2-WO3 is a promising candidate for indoor formaldehyde treatment in practical applications.
TiO2-WO3 Loaded onto Wood Surface for Photocatalytic Degradation of Formaldehyde
In this work, a facile method was adopted to prepare TiO2-WO3 loaded onto a wood surface by a two-step hydrothermal method. The as-prepared wood composite material can be used as a photocatalyst under UV irradiation for the photodegradation of formaldehyde. Related tests showed that TiO2-WO3 nano-architectonic materials with spherical particles loaded onto the wood substratewere mainly caused by self-photodegradation of formaldehyde. The TiO2-WO3 nanostructured material firmly adheres to the wood substrate through electrostatic and hydrogen bonding interactions. Meanwhile, the appearance of the new chemical bond Ti-O-W indicates the successful loading of TiO2-WO3 onto the wood surface. The photodegradation rate was measured and it was confirmed that the highest photodegradation performance of the modified wood was achieved at a molar ratio of 5:1 of TiO2 to WO3. This work provides a new strategy for the preparing of novel photocatalysts based on wood substrate. Moreover, the wood loaded with TiO2-WO3 is a promising candidate for indoor formaldehyde treatment in practical applications.
TiO2-WO3 Loaded onto Wood Surface for Photocatalytic Degradation of Formaldehyde
Song Li (Autor:in) / Zequn Li (Autor:in) / Luming Li (Autor:in) / Xiangdong Dai (Autor:in) / Meiling Chen (Autor:in) / Wenkai Zhu (Autor:in)
2023
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
| British Library Online Contents | 2017
| British Library Online Contents | 2012
Photocatalytic degradation of vehicle exhaust using Fe-doped TiO2 loaded on activated carbon
| British Library Online Contents | 2017