Analyses of Sulfur and Iron in Waterlogged Archaeological Wood: The Case of Polyethylene-Glycol-Treated Yenikapı 12 Shipwreck
The Yenikapı (YK) 12 shipwreck is 1 of 37 shipwrecks found at Yenikapı, Istanbul. This merchantman has been dated to AD 672–876 by radiocarbon analyses. The conservation of YK 12, which was assembled with iron nails, was completed with the pre-impregnation of polyethylene glycol (PEG) and using vacuum freeze-drying processes. However, after conservation, dust formation was observed on some wooden parts of the shipwreck during storage. In this study, iron–sulfur-related problems detected in the woods of YK 12 were evaluated. We analysed samples taken from YK 12 to study the sulfur and iron content in woods from oak (Quercus), walnut (Juglans), and hornbeam (Carpinus), representing taxa with different wood properties. Fourier-transform infrared spectroscopy (FTIR) analyses, X-ray diffraction (XRD), and pH measurements were conducted on five samples. The results of these studies showed that the dust consisted of wood particles, PEG, and hydrated iron sulfates, such as FeSO4·4H2O and FeSO4·7H2O. Additionally, one sample included SiO2, whilst another exhibited a low pH value. These findings highlight the importance of optimum ambient conditions for the storage and display of these shipwrecks in order to prevent the irreversible degradation of YK 12 and other recovered shipwrecks.
Analyses of Sulfur and Iron in Waterlogged Archaeological Wood: The Case of Polyethylene-Glycol-Treated Yenikapı 12 Shipwreck
The Yenikapı (YK) 12 shipwreck is 1 of 37 shipwrecks found at Yenikapı, Istanbul. This merchantman has been dated to AD 672–876 by radiocarbon analyses. The conservation of YK 12, which was assembled with iron nails, was completed with the pre-impregnation of polyethylene glycol (PEG) and using vacuum freeze-drying processes. However, after conservation, dust formation was observed on some wooden parts of the shipwreck during storage. In this study, iron–sulfur-related problems detected in the woods of YK 12 were evaluated. We analysed samples taken from YK 12 to study the sulfur and iron content in woods from oak (Quercus), walnut (Juglans), and hornbeam (Carpinus), representing taxa with different wood properties. Fourier-transform infrared spectroscopy (FTIR) analyses, X-ray diffraction (XRD), and pH measurements were conducted on five samples. The results of these studies showed that the dust consisted of wood particles, PEG, and hydrated iron sulfates, such as FeSO4·4H2O and FeSO4·7H2O. Additionally, one sample included SiO2, whilst another exhibited a low pH value. These findings highlight the importance of optimum ambient conditions for the storage and display of these shipwrecks in order to prevent the irreversible degradation of YK 12 and other recovered shipwrecks.
Analyses of Sulfur and Iron in Waterlogged Archaeological Wood: The Case of Polyethylene-Glycol-Treated Yenikapı 12 Shipwreck
Aslı Gökçe Kılıç (Autor:in) / Namık Kılıç (Autor:in) / Donna C. Arnold (Autor:in)
2023
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
| DOAJ | 2023
| DOAJ | 2021
Chemical Characterization of Waterlogged Charred Wood: The Case of a Medieval Shipwreck
| DOAJ | 2021
The Viscoelastic Behaviour of Waterlogged Archaeological Wood Treated with Methyltrimethoxysilane
| BASE | 2021