Positron lifetime study of ion-irradiated tungsten: Ion type and dose effects
Polycrystalline recrystallized tungsten samples were irradiated with 7.5 MeV Si ions and 9 MeV Cu ions to three different damage levels (0.01, 0.1, 0.5 dpa at 200 nm depth) at 295 K. The resulting vacancy-type defects in the samples were studied using positron annihilation lifetime spectroscopy. The dependence of the average positron lifetime on the damage level is found to be non-linear: a steep increase at low damage levels with a tendency to saturation at higher damage levels (>0.1 dpa). The average positron lifetime of Si and Cu-irradiated tungsten is very similar at each damage level, suggesting similar vacancy-type defect structure. Deconvolution of the positron lifetime spectra revealed that the dominant irradiation-induced defect type is a single vacancy. The presence of small vacancy clusters is also detected. Their fraction is found to increase with increasing damage level.
Positron lifetime study of ion-irradiated tungsten: Ion type and dose effects
Polycrystalline recrystallized tungsten samples were irradiated with 7.5 MeV Si ions and 9 MeV Cu ions to three different damage levels (0.01, 0.1, 0.5 dpa at 200 nm depth) at 295 K. The resulting vacancy-type defects in the samples were studied using positron annihilation lifetime spectroscopy. The dependence of the average positron lifetime on the damage level is found to be non-linear: a steep increase at low damage levels with a tendency to saturation at higher damage levels (>0.1 dpa). The average positron lifetime of Si and Cu-irradiated tungsten is very similar at each damage level, suggesting similar vacancy-type defect structure. Deconvolution of the positron lifetime spectra revealed that the dominant irradiation-induced defect type is a single vacancy. The presence of small vacancy clusters is also detected. Their fraction is found to increase with increasing damage level.
Positron lifetime study of ion-irradiated tungsten: Ion type and dose effects
B. Wieluńska-Kuś (Autor:in) / M. Dickmann (Autor:in) / W. Egger (Autor:in) / M. Zibrov (Autor:in) / Ł. Ciupiński (Autor:in)
2024
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Positron lifetime study of ion-irradiated tungsten: Ion type and dose effects
| Elsevier | 2024
Positron Lifetime Study of Gamma Irradiated Rochelle Salt
| British Library Online Contents | 1997
Positron Annihilation Lifetime of Irradiated Polyimide
| British Library Online Contents | 2013
The Study of Positron Lifetime in Neutron Irradiated GaAs
| British Library Online Contents | 1995
Positron Annihilation Lifetime Study of Irradiated Fe-Cu Allloys
| British Library Online Contents | 1995