Performance of Self-healing Cementitious Mortar with PVA Fiber and SAP
Abstract Although concrete materials generally exhibit outstanding mechanical properties, it is susceptible against crack formation. It has been reported that narrow cracks (≤ 150 µm) could be naturally sealed in the cement matrix by externally supplied water-induced hydration. However, the crack width of larger than 150 µm is difficult to be sealed without using additional self-healing admixture. In this study, the self-healing cementitious mortar was successfully developed by using a combination of polyvinyl alcohol (PVA) fiber and superabsorbent polymer (SAP), aiming to heal the wide cracks. Although the mechanical properties were slightly reduced, it shows outstanding self-healing performance by using the dual admixtures. A self-healing rate of 60% was observed in the control sample with an initial crack width of 300 µm, while a self-healing rate of nearly 100% was confirmed with suitable SAP and PVA. In addition, it was confirmed that lower hydration degree of self-healing mortar in early stage contributes to the enhanced self-healing performance of developed composite system by internally supplied water from SAP.
Performance of Self-healing Cementitious Mortar with PVA Fiber and SAP
Abstract Although concrete materials generally exhibit outstanding mechanical properties, it is susceptible against crack formation. It has been reported that narrow cracks (≤ 150 µm) could be naturally sealed in the cement matrix by externally supplied water-induced hydration. However, the crack width of larger than 150 µm is difficult to be sealed without using additional self-healing admixture. In this study, the self-healing cementitious mortar was successfully developed by using a combination of polyvinyl alcohol (PVA) fiber and superabsorbent polymer (SAP), aiming to heal the wide cracks. Although the mechanical properties were slightly reduced, it shows outstanding self-healing performance by using the dual admixtures. A self-healing rate of 60% was observed in the control sample with an initial crack width of 300 µm, while a self-healing rate of nearly 100% was confirmed with suitable SAP and PVA. In addition, it was confirmed that lower hydration degree of self-healing mortar in early stage contributes to the enhanced self-healing performance of developed composite system by internally supplied water from SAP.
Performance of Self-healing Cementitious Mortar with PVA Fiber and SAP
Sukmin Kwon (Autor:in) / Sugyu Lee (Autor:in) / Hyunuk Kang (Autor:in) / Min Kyoung Kim (Autor:in) / Sungwun Her (Autor:in) / Sungchul Bae (Autor:in) / Dong Joo Kim (Autor:in) / Juhyuk Moon (Autor:in)
2024
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Performance of Self-healing Cementitious Mortar with PVA Fiber and SAP
| Springer Verlag | 2024
Performance of Self-healing Cementitious Mortar with PVA Fiber and SAP
| Springer Verlag | 2024
Self-healing of bio-cementitious mortar incubated within neutral and acidic soil
| Online Contents | 2021
| DOAJ | 2023
Self-healing of bio-cementitious mortar incubated within neutral and acidic soil
| Springer Verlag | 2021