Strength Properties of Various Types of Fiber-Reinforced Concrete for Production of Driven Piles
This paper presents the results of static and dynamic tests of fiber-reinforced and unreinforced concrete samples under laboratory conditions. Concrete samples reinforced with steel and non steel fibers were tested. The dynamic tests were carried out on the stand by applying falling weight impacts on the concrete samples. The impact testing of samples included two stages of deformation: until the first defects appeared in the samples and until their complete destruction. The impact resistance of the samples was evaluated according to the energy input of the hammer with registration of the type, size and volume of the defects. It was revealed that the type of fibers has a different effect on the static and impact resistance of fiber concrete. Correlational dependencies used for predicting the strength and energy parameters of fiber concrete in their comparative evaluation have been obtained. It has been determined that the static strength and impact resistance of fiber concrete may not be identical, i.e., a high static strength in fiber concrete does not always provide a high impact resistance. The impact resistance of fiber concrete when tested before the first defects appear is always lower than when tested before complete failure.
Strength Properties of Various Types of Fiber-Reinforced Concrete for Production of Driven Piles
This paper presents the results of static and dynamic tests of fiber-reinforced and unreinforced concrete samples under laboratory conditions. Concrete samples reinforced with steel and non steel fibers were tested. The dynamic tests were carried out on the stand by applying falling weight impacts on the concrete samples. The impact testing of samples included two stages of deformation: until the first defects appeared in the samples and until their complete destruction. The impact resistance of the samples was evaluated according to the energy input of the hammer with registration of the type, size and volume of the defects. It was revealed that the type of fibers has a different effect on the static and impact resistance of fiber concrete. Correlational dependencies used for predicting the strength and energy parameters of fiber concrete in their comparative evaluation have been obtained. It has been determined that the static strength and impact resistance of fiber concrete may not be identical, i.e., a high static strength in fiber concrete does not always provide a high impact resistance. The impact resistance of fiber concrete when tested before the first defects appear is always lower than when tested before complete failure.
Strength Properties of Various Types of Fiber-Reinforced Concrete for Production of Driven Piles
Bekbasarov Isabai (Autor:in) / Shanshabayev Nurzhan (Autor:in) / Atenov Yerlan (Autor:in)
2023
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Driven steel-fiber-reinforced-concrete pyramidal piles
| Online Contents | 1984
Effectiveness of use of steel-fiber concrete in reinforced concrete driven piles
| Online Contents | 1985
Impact-Driven Penetration of Multi-Strength Fiber Concrete Pyramid-Prismatic Piles
| DOAJ | 2024
| Engineering Index Backfile | 1947
| British Library Conference Proceedings | 2002