Porosity and Mechanical Strength of an Autoclaved Clayey Cellular Concrete
This paper investigates the porosity and the mechanical strength of an Autoclaved Clayey Cellular Concrete (ACCC) with the binder produced with 75 wt% kaolinite clay and 25 wt% Portland cement. Aluminum powder was used as foaming agent, from 0.2 wt% to 0.8 wt%, producing specimens with different porosities. The results show that the specimens with higher content of aluminum presented pore coalescence, which can explain the lower porosity of these samples. The porosities obtained with the aluminum contents used in the study were high (approximately 80%), what accounts for the low mechanical strength of the investigated cellular concretes (maximum of 0.62 MPa). Nevertheless, comparing the results obtained in this study to the ones for low temperature clayey aerated concrete with similar compositions, it can be observed that autoclaving is effective for increasing the material mechanical strength.
Porosity and Mechanical Strength of an Autoclaved Clayey Cellular Concrete
This paper investigates the porosity and the mechanical strength of an Autoclaved Clayey Cellular Concrete (ACCC) with the binder produced with 75 wt% kaolinite clay and 25 wt% Portland cement. Aluminum powder was used as foaming agent, from 0.2 wt% to 0.8 wt%, producing specimens with different porosities. The results show that the specimens with higher content of aluminum presented pore coalescence, which can explain the lower porosity of these samples. The porosities obtained with the aluminum contents used in the study were high (approximately 80%), what accounts for the low mechanical strength of the investigated cellular concretes (maximum of 0.62 MPa). Nevertheless, comparing the results obtained in this study to the ones for low temperature clayey aerated concrete with similar compositions, it can be observed that autoclaving is effective for increasing the material mechanical strength.
Porosity and Mechanical Strength of an Autoclaved Clayey Cellular Concrete
P. O. Guglielmi (Autor:in) / W. R. L. Silva (Autor:in) / W. L. Repette (Autor:in) / D. Hotza (Autor:in)
2010
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
| British Library Online Contents | 1992
Porosity and permeability of autoclaved aerated concrete
| British Library Conference Proceedings | 1992
Non-autoclaved high strength cellular concrete from alkali activated slag
| British Library Online Contents | 2012
Non-autoclaved high strength cellular concrete from alkali activated slag
| Online Contents | 2012