INFLUENCE OF ECAP TEMPERATURE ON THE MECHANICAL PROPERTIES OF PURE TI

DU FeiPeng / LIU Fang / JIAO QingYa / WANG Fei

Commercial pure titanium（ CP-Ti） TA2 was pressed 1 pass by equal channel angular pressing（ ECAP） with BC route at room temperature（ RT） and 300℃,respectively. The microstructure and mechanical properties of the samples were investigated to find the influence of ECAP temperature on the mechanical properties of CP-Ti. The experimental results suggested that grains of the samples after ECAP 1 pass were elongated and lath-like and crystal twinning was found,the microhardness and tensile strength of the samples pressed 1 pass at room temperature and 300℃ increased from 179. 5 kgf·mm^-2,443 MPa to 234. 2 kgf·mm^-2,560 MPa and 213. 5 kgf·mm^-2、544 MPa,respectively,while the elongation at break reduced from 21. 5% to 11. 5% and 16. 5%,respectively.

Zugriff

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

INFLUENCE OF ECAP TEMPERATURE ON THE MECHANICAL PROPERTIES OF PURE TI

DU FeiPeng / LIU Fang / JIAO QingYa / WANG Fei

Commercial pure titanium（ CP-Ti） TA2 was pressed 1 pass by equal channel angular pressing（ ECAP） with BC route at room temperature（ RT） and 300℃,respectively. The microstructure and mechanical properties of the samples were investigated to find the influence of ECAP temperature on the mechanical properties of CP-Ti. The experimental results suggested that grains of the samples after ECAP 1 pass were elongated and lath-like and crystal twinning was found,the microhardness and tensile strength of the samples pressed 1 pass at room temperature and 300℃ increased from 179. 5 kgf·mm^-2,443 MPa to 234. 2 kgf·mm^-2,560 MPa and 213. 5 kgf·mm^-2、544 MPa,respectively,while the elongation at break reduced from 21. 5% to 11. 5% and 16. 5%,respectively.

INFLUENCE OF ECAP TEMPERATURE ON THE MECHANICAL PROPERTIES OF PURE TI

DU FeiPeng / LIU Fang / JIAO QingYa / WANG Fei

Commercial pure titanium（ CP-Ti） TA2 was pressed 1 pass by equal channel angular pressing（ ECAP） with BC route at room temperature（ RT） and 300℃,respectively. The microstructure and mechanical properties of the samples were investigated to find the influence of ECAP temperature on the mechanical properties of CP-Ti. The experimental results suggested that grains of the samples after ECAP 1 pass were elongated and lath-like and crystal twinning was found,the microhardness and tensile strength of the samples pressed 1 pass at room temperature and 300℃ increased from 179. 5 kgf·mm^-2,443 MPa to 234. 2 kgf·mm^-2,560 MPa and 213. 5 kgf·mm^-2、544 MPa,respectively,while the elongation at break reduced from 21. 5% to 11. 5% and 16. 5%,respectively.

Zugriff

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

INFLUENCE OF ECAP TEMPERATURE ON THE MECHANICAL PROPERTIES OF PURE TI

Beteiligte:

DU FeiPeng (Autor:in) / LIU Fang (Autor:in) / JIAO QingYa (Autor:in) / WANG Fei (Autor:in)

Erschienen in:

Jixie qiangdu, Vol 39, Pp 692-696 (2017)

Erscheinungsdatum:

2017

ISSN:

Medientyp:

Aufsatz (Zeitschrift)

Format:

Elektronische Ressource

Sprache:

Unbekannt

Schlagwörter:

Equal channel angular pressing（ECAP） , CP-Ti , Temperature , Microstructure , Mechanical properties , Mechanical engineering and machinery , TJ1-1570 , Materials of engineering and construction. Mechanics of materials , TA401-492

Metadata by DOAJ is licensed under CC BY-SA 1.0

Ähnliche Titel

Influence of ECAP routes on the microstructure and properties of pure Ti

Stolyarov, V. V. / Zhu, Y. T. / Alexandrov, I. V. et al. | British Library Online Contents | 2001

Microstructure and Properties of Commercial Pure Titanium Processed by ECAP at Room Temperature

Wang, C. / Zhao, X.-c. / Yang, X.-r. et al. | British Library Online Contents | 2009

Grain Refinement of Pure Copper by ECAP

Lugo, N. / Cabrera, J.M. / Llorca, N. et al. | British Library Online Contents | 2008

Thermal stability of ECAP processed pure copper

Molodova, X. / Gottstein, G. / Winning, M. et al. | British Library Online Contents | 2007

Improved mechanical property and internal friction of pure Mg processed by ECAP

Fan, G. D. / Zheng, M. Y. / Hu, X. S. et al. | British Library Online Contents | 2012