Irradiation hardening behaviors of large-scale hot rolling potassium-doped tungsten alloy under synergistic irradiations of Fe11+ ion combined with deuterium and helium plasmas
In this study, a 25 kg potassium doped tungsten (KW) plate dispersed K bubbles was prepared by hot rolling firstly. In order to evaluate the mechanical properties of KW after irradiation, the synergistic irradiation of Fe11+ ion, He and D plasmas were performed on KW and pure tungsten (PW). 3.5-MeV Fe11+ ion irradiation was used to simulate displacement damage induced by neutrons. The total fluence and irradiation temperature were 5.31 × 1014 m−2 for 0.5 displacements per atom (dpa) damage and 400 K, respectively. Positron annihilation Doppler broadening spectrometry (PA-DBS) technique was applied to measure the type of defect in both undamaged and damaged PW & KW samples. The total ion fluence helium (He) and deuterium (D) were kept constant at 1 × 1025 He m−2 and 5 × 1024 D m−2, separately. Subsequently, the hardness value of PW and KW received from CSM nanoindentation technique was analyzed and compared. The results show that the increase of vacancy-type defects in KW is restrained after irradiation compared with PW. For un-irradiated PW and KW samples, there are almost the same pop-in events, which indicate that PW and KW a similar plastic deformation at room temperature. The KW shows a better irradiation hardening resistance than PW under the same irradiation condition. Besides, the evolution of irradiation hardening as well as their relationship with K bubbles were discussed in detail.
Irradiation hardening behaviors of large-scale hot rolling potassium-doped tungsten alloy under synergistic irradiations of Fe11+ ion combined with deuterium and helium plasmas
In this study, a 25 kg potassium doped tungsten (KW) plate dispersed K bubbles was prepared by hot rolling firstly. In order to evaluate the mechanical properties of KW after irradiation, the synergistic irradiation of Fe11+ ion, He and D plasmas were performed on KW and pure tungsten (PW). 3.5-MeV Fe11+ ion irradiation was used to simulate displacement damage induced by neutrons. The total fluence and irradiation temperature were 5.31 × 1014 m−2 for 0.5 displacements per atom (dpa) damage and 400 K, respectively. Positron annihilation Doppler broadening spectrometry (PA-DBS) technique was applied to measure the type of defect in both undamaged and damaged PW & KW samples. The total ion fluence helium (He) and deuterium (D) were kept constant at 1 × 1025 He m−2 and 5 × 1024 D m−2, separately. Subsequently, the hardness value of PW and KW received from CSM nanoindentation technique was analyzed and compared. The results show that the increase of vacancy-type defects in KW is restrained after irradiation compared with PW. For un-irradiated PW and KW samples, there are almost the same pop-in events, which indicate that PW and KW a similar plastic deformation at room temperature. The KW shows a better irradiation hardening resistance than PW under the same irradiation condition. Besides, the evolution of irradiation hardening as well as their relationship with K bubbles were discussed in detail.
Irradiation hardening behaviors of large-scale hot rolling potassium-doped tungsten alloy under synergistic irradiations of Fe11+ ion combined with deuterium and helium plasmas
Xiaolei Ma (Autor:in) / Xiaoxin Zhang (Autor:in) / Ting Wang (Autor:in) / Wei Lv (Autor:in) / Shaoting Lang (Autor:in) / Changchun Ge (Autor:in) / Qingzhi Yan (Autor:in)
2022
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Effect of 3 MeV Fe11+ ions pre-damage on blistering and deuterium retention in two tungsten grades
| DOAJ | 2021
Deuterium and helium ion irradiation of nanograined tungsten and tungsten–titanium alloys
| DOAJ | 2019
| Elsevier | 2024