Proton and Au-ion irradiation induced damage and hardening in ferritic/martensitic steel
Ferritic/martensitic (F/M) steel was irradiated by proton and Au-ion at 400 °C to investigate the irradiation damage and hardening behavior. For the samples irradiated by proton, dislocation loops and dislocation lines were found in F/M steels and the proton irradiation induced dislocation loops were mostly a0 〈1 0 0〉 type with a few 1/2a0 〈1 1 1〉 type. For the samples irradiated by Au-ion, many voids were found in F/M steels and the void size increased with the increasing irradiation depth (0–420 nm). The void density climb up and then decline with the irradiation depth increasing from 0 nm to 450 nm. The damage distribution under proton and Au-ion irradiation were accorded well with the calculation results by SRIM. In addition, hardening effects happened in both proton and Au-ion irradiated F/M steels.
Proton and Au-ion irradiation induced damage and hardening in ferritic/martensitic steel
Ferritic/martensitic (F/M) steel was irradiated by proton and Au-ion at 400 °C to investigate the irradiation damage and hardening behavior. For the samples irradiated by proton, dislocation loops and dislocation lines were found in F/M steels and the proton irradiation induced dislocation loops were mostly a0 〈1 0 0〉 type with a few 1/2a0 〈1 1 1〉 type. For the samples irradiated by Au-ion, many voids were found in F/M steels and the void size increased with the increasing irradiation depth (0–420 nm). The void density climb up and then decline with the irradiation depth increasing from 0 nm to 450 nm. The damage distribution under proton and Au-ion irradiation were accorded well with the calculation results by SRIM. In addition, hardening effects happened in both proton and Au-ion irradiated F/M steels.
Proton and Au-ion irradiation induced damage and hardening in ferritic/martensitic steel
Ke Shi (Autor:in) / Wei Zhang (Autor:in) / Zhien Ning (Autor:in) / Hui Wang (Autor:in) / Jiali Liao (Autor:in) / Yuanyou Yang (Autor:in) / Ning Liu (Autor:in) / Jijun Yang (Autor:in)
2021
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Modeling of radiation hardening in ferritic/martensitic steel using multi-scale approach
| British Library Online Contents | 2012
Fatigue properties of ferritic/martensitic steel after neutron irradiation and helium implantation
| DOAJ | 2020
Irradiation Effects on Precipitation in Reduced-Activation Ferritic/Martensitic Steels
| British Library Online Contents | 2005
Abnormal Grain Growth in Ferritic-Martensitic Eurofer-97 Steel
| British Library Online Contents | 2013