Effect of Aging on Fracture Toughness of Al6061-Graphite Particulate Composites
This article presents the investigative work conducted on the fracture toughness and microstructure of Al6061-9% graphite particulate composites. The requisite specimens for the fracture toughness testing were compact tension ones prepared using stir casting technique. The Al6061-9% graphite particulate metal matrix composite has been heat treated in the underaged condition. It is observed from the results that as aging time increases, the fracture toughness increases. This gain in fracture toughness is with the loss of ductility. Examination of the fractured surface of Al6061-graphite is done using a scanning electron microscope (SEM) which shows the brittle fracture of the composite.
Effect of Aging on Fracture Toughness of Al6061-Graphite Particulate Composites
This article presents the investigative work conducted on the fracture toughness and microstructure of Al6061-9% graphite particulate composites. The requisite specimens for the fracture toughness testing were compact tension ones prepared using stir casting technique. The Al6061-9% graphite particulate metal matrix composite has been heat treated in the underaged condition. It is observed from the results that as aging time increases, the fracture toughness increases. This gain in fracture toughness is with the loss of ductility. Examination of the fractured surface of Al6061-graphite is done using a scanning electron microscope (SEM) which shows the brittle fracture of the composite.
Effect of Aging on Fracture Toughness of Al6061-Graphite Particulate Composites
Saleemsab Doddamani (Autor:in) / Mohamed Kaleemulla K (Autor:in)
2019
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
The sliding wear behavior of Al6061-garnet particulate composites
| British Library Online Contents | 2001
Toughness enhancement in architecturally modified Al6061-5 vol.% SiCp laminated composites
| British Library Online Contents | 2015
Interlaminar Fracture Toughness of Graphite Fiber-Reinforced Polyimide Composites
| British Library Online Contents | 1994
High-rate fracture toughness of polypropylene-based, hybrid, particulate composites
| British Library Online Contents | 1994