Damage Strengthening Constitutive Model of Cemented Paste Backfill
In order to consider the influence of mesoscopic characteristics of materials on the constitutive model of cemented paste backfill (CPB), the uniaxial compression variables and the damage constitutive model, considering the influence of porosity and pore size of filling materials, were derived based on the strain equivalence principle and Weibull probability distribution function. The nuclear magnetic resonance (NMR) tests and unconfined compression strength (UCS) tests were carried out on 8 groups of CPB specimens with different slurry concentrations and cement-tailings ratios. Then, the expression of damage strengthening coefficient is determined, and the stress-strain curves measured by the theoretical model were compared with the experimental ones. The results show that the uniaxial compression constitutive model proposed is in good agreement with UCS test results and can effectively describe the damage evolution law and the development process of stress-strain curve of CPB under uniaxial compression. The 28-day compressive strength of CPB can reach 8 MPa, the residual strength is about 1∼2 MPa, the elastic modulus is about 200∼2000 MPa, and the porosity is about 3∼5%. The CPB with slurry concentration of 74% and 76% and cement-tailings ratio of 1 : 4 and 1 : 6 is more reasonable, and the relevant mechanical parameters are more stable.
Damage Strengthening Constitutive Model of Cemented Paste Backfill
In order to consider the influence of mesoscopic characteristics of materials on the constitutive model of cemented paste backfill (CPB), the uniaxial compression variables and the damage constitutive model, considering the influence of porosity and pore size of filling materials, were derived based on the strain equivalence principle and Weibull probability distribution function. The nuclear magnetic resonance (NMR) tests and unconfined compression strength (UCS) tests were carried out on 8 groups of CPB specimens with different slurry concentrations and cement-tailings ratios. Then, the expression of damage strengthening coefficient is determined, and the stress-strain curves measured by the theoretical model were compared with the experimental ones. The results show that the uniaxial compression constitutive model proposed is in good agreement with UCS test results and can effectively describe the damage evolution law and the development process of stress-strain curve of CPB under uniaxial compression. The 28-day compressive strength of CPB can reach 8 MPa, the residual strength is about 1∼2 MPa, the elastic modulus is about 200∼2000 MPa, and the porosity is about 3∼5%. The CPB with slurry concentration of 74% and 76% and cement-tailings ratio of 1 : 4 and 1 : 6 is more reasonable, and the relevant mechanical parameters are more stable.
Damage Strengthening Constitutive Model of Cemented Paste Backfill
Kangli Cheng (Autor:in) / Bingbing Tu (Autor:in) / Lang Liu (Autor:in) / Bo Zhang (Autor:in) / Huafu Qiu (Autor:in)
2021
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
| DOAJ | 2016
| DOAJ | 2022
Constitutive modelling of cemented paste backfill: A data-mining approach
| British Library Online Contents | 2019