Durability of binders, mortars and concretes in aggressive environments is of crucial importance for their commercial application. In this paper the resistance to external sulfate attack of two different alkaliactivated binders (AABs), based either on blast furnace slag (BFS) or fly ash/blast furnace slag (FA/BFS) blend, was compared with two different commercially available Portland cement (CEM II) blended either with BFS or with FA and BFS. Comparison of sulfate resistance was based on compressive strength testing (the loss of strength) of mortar samples exposed to sodium sulfate attack up to 180 days and samples cured under controlled conditions for the same period of time. Furthermore, the evolution of microstructure of alkali-activated binders and pH of sodium silicate solution during testing were also analyzed. Despite different gel chemistry being involved, both alkali-activated binders based either on BFS or FA/BFS blend showed excellent resistance to external sulfate attack and even better than selected Portland cements tested under the same experimental conditions.
Resistance to external sulfate attack - Comparison of two alkali-activated binders
Durability of binders, mortars and concretes in aggressive environments is of crucial importance for their commercial application. In this paper the resistance to external sulfate attack of two different alkaliactivated binders (AABs), based either on blast furnace slag (BFS) or fly ash/blast furnace slag (FA/BFS) blend, was compared with two different commercially available Portland cement (CEM II) blended either with BFS or with FA and BFS. Comparison of sulfate resistance was based on compressive strength testing (the loss of strength) of mortar samples exposed to sodium sulfate attack up to 180 days and samples cured under controlled conditions for the same period of time. Furthermore, the evolution of microstructure of alkali-activated binders and pH of sodium silicate solution during testing were also analyzed. Despite different gel chemistry being involved, both alkali-activated binders based either on BFS or FA/BFS blend showed excellent resistance to external sulfate attack and even better than selected Portland cements tested under the same experimental conditions.
Resistance to external sulfate attack - Comparison of two alkali-activated binders
Komljenović Miroslav (Autor:in) / Džunuzović Nataša (Autor:in) / Nikolić Violeta (Autor:in)
2018
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
External sulfate attack: comparison of several alternative binders
| Online Contents | 2021
External sulfate attack: comparison of several alternative binders
| Springer Verlag | 2021
External sulfate attack on alkali-activated slag
| British Library Online Contents | 2013
External sulfate attack on alkali-activated slag
| Online Contents | 2013
External sulfate attack on alkali-activated fly ash-blast furnace slag composite
| British Library Online Contents | 2017