Chemical Composition as the Indicator of Thermally Treated Pine (Pinus sylvestris L.) Wood Colour
This study aimed to determine the influence of increased temperature on the mass loss, chemical composition, and colour of pine wood because of the lack of such information. The colour was measured on samples of wood, extracted sawdust, holocellulose, and lignin isolated from the extracted sawdust of pine heartwood and sapwood. A wood sample labelled 20 °C was considered as wood with the original composition. Subsequently, we verified the measured values with the proposed mixing colour model. Pine heartwood and sapwood samples were thermally treated at temperatures of 100, 150, 200, 220, 240, and 260 °C for 1, 3, and 5 h. It was found that sapwood degraded faster than heartwood. The thermal treatment of wood increases lignin content and decreases holocellulose content, especially at 260 °C. The maximum extractive content of 3.60% was at 1 h and a temperature of 260 °C for both parts of the wood. Lightness values decreased with increasing temperature and time of treatment. The coordinate a* of heartwood showed a positive slope until one hour of treatment duration and a temperature of 240 °C. Then, it decreased for the subsequent duration of treatment. The same course was shown for the coordinate b* of sapwood at a temperature of 200 °C. The proposed model of mixing colours proved that changes in both parts of a wood-extracted substance, holocellulose, and lignin content, were responsible for the changing colour of extracted wood.
Chemical Composition as the Indicator of Thermally Treated Pine (Pinus sylvestris L.) Wood Colour
This study aimed to determine the influence of increased temperature on the mass loss, chemical composition, and colour of pine wood because of the lack of such information. The colour was measured on samples of wood, extracted sawdust, holocellulose, and lignin isolated from the extracted sawdust of pine heartwood and sapwood. A wood sample labelled 20 °C was considered as wood with the original composition. Subsequently, we verified the measured values with the proposed mixing colour model. Pine heartwood and sapwood samples were thermally treated at temperatures of 100, 150, 200, 220, 240, and 260 °C for 1, 3, and 5 h. It was found that sapwood degraded faster than heartwood. The thermal treatment of wood increases lignin content and decreases holocellulose content, especially at 260 °C. The maximum extractive content of 3.60% was at 1 h and a temperature of 260 °C for both parts of the wood. Lightness values decreased with increasing temperature and time of treatment. The coordinate a* of heartwood showed a positive slope until one hour of treatment duration and a temperature of 240 °C. Then, it decreased for the subsequent duration of treatment. The same course was shown for the coordinate b* of sapwood at a temperature of 200 °C. The proposed model of mixing colours proved that changes in both parts of a wood-extracted substance, holocellulose, and lignin content, were responsible for the changing colour of extracted wood.
Chemical Composition as the Indicator of Thermally Treated Pine (Pinus sylvestris L.) Wood Colour
Viera Kučerová (Autor:in) / Richard Hrčka (Autor:in) / Tatiana Hýrošová (Autor:in)
2024
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
pine , thermal treatment , colour , holocellulose , lignin , extractives , Plant ecology , QK900-989
Metadata by DOAJ is licensed under CC BY-SA 1.0
| British Library Online Contents | 2016
Analysis of Deformation Fixation of Thermally Compressed Scots Pine (Pinus sylvestris L.)
| DOAJ | 2024
Effects of the wood preservatives on mechanical properties of yellow pine (Pinus sylvestris L.) wood
| Online Contents | 2004
Effects of the wood preservatives on mechanical properties of yellow pine (Pinus sylvestris L.) wood
| British Library Online Contents | 2004