Influence Of Volcanic Scoria On Mechanical Strength, Chemical Resistance And Drying Shrinkage Of Mortars
In the study, three types of cement have been prepared; one CEM I type (the control sample) and two blended cements: CEM II/A-P and CEM II/B-P (EN 197-1), each of them with three replacement levels of volcanic scoria: (10 %, 15 %, 20 % wt.) and (25 %, 30 %, 35 % wt.), respectively. Strength development of mortars has been investigated at 2, 7, 28 and 90 days curing. Evaluation of chemical resistance of mortars containing scoria-based cements has been investigated through exposure to 5 % sulphate and 5 % sulphuric acid solutions in accordance with ASTM C1012 & ASTM 267, respectively. Drying shrinkage has been evaluated in accordance with ASTM C596. Test results showed that at early ages, the mortars containing CEM II/B-P binders had strengths much lower than that of the control mortar. However, at 90 days curing, the strengths were comparable to the control mortar. In addition, the increase of scoria significantly improved the sulphate resistance of mortars. Further, an increase in scoria addition improved the sulphuric acid resistance of mortar, especially at the early days of exposure. The results of drying shrinkage revealed that the CEM II/B-P mortar bars exhibited a greater contraction when compared to the control mortar, especially at early ages. However, drying shrinkage of mortars was not influenced much at longer times.
Influence Of Volcanic Scoria On Mechanical Strength, Chemical Resistance And Drying Shrinkage Of Mortars
In the study, three types of cement have been prepared; one CEM I type (the control sample) and two blended cements: CEM II/A-P and CEM II/B-P (EN 197-1), each of them with three replacement levels of volcanic scoria: (10 %, 15 %, 20 % wt.) and (25 %, 30 %, 35 % wt.), respectively. Strength development of mortars has been investigated at 2, 7, 28 and 90 days curing. Evaluation of chemical resistance of mortars containing scoria-based cements has been investigated through exposure to 5 % sulphate and 5 % sulphuric acid solutions in accordance with ASTM C1012 & ASTM 267, respectively. Drying shrinkage has been evaluated in accordance with ASTM C596. Test results showed that at early ages, the mortars containing CEM II/B-P binders had strengths much lower than that of the control mortar. However, at 90 days curing, the strengths were comparable to the control mortar. In addition, the increase of scoria significantly improved the sulphate resistance of mortars. Further, an increase in scoria addition improved the sulphuric acid resistance of mortar, especially at the early days of exposure. The results of drying shrinkage revealed that the CEM II/B-P mortar bars exhibited a greater contraction when compared to the control mortar, especially at early ages. However, drying shrinkage of mortars was not influenced much at longer times.
Influence Of Volcanic Scoria On Mechanical Strength, Chemical Resistance And Drying Shrinkage Of Mortars
Al-Swaidani A. (Autor:in) / Aliyan S. (Autor:in) / Adarnaly N. (Autor:in) / Hanna B. (Autor:in) / Dyab E. (Autor:in)
2014
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Properties of volcanic scoria based lightweight concrete
| Online Contents | 2004
DRYING SHRINKAGE AND STRENGTH PROPERTIES OF REDISPERSIBLE POLYMER POWDER-MODIFIED MORTARS
| British Library Conference Proceedings | 2005
Particle Density of Volcanic Scoria Determined by Water Pycnometry
| British Library Online Contents | 2005
Particle Density of Volcanic Scoria Determined by Water Pycnometry
| Online Contents | 2005