Reactivity of high alumina cement in water: Pore solution and solid phase characterization
The hydration reaction of high alumina cement at a temperature of 20 ºC and water/cement ratio of 0.5 has been studied over a period of one month. The changes of the solid phase were followed by X-ray diffraction and thermal analysis. Besides, pore-solution was expressed by application of high mechanical pressure (500 MPa) during different periods of the reaction in order to study its Chemical composition evolution as a result of the hydration process.
Reactivity of high alumina cement in water: Pore solution and solid phase characterization
The hydration reaction of high alumina cement at a temperature of 20 ºC and water/cement ratio of 0.5 has been studied over a period of one month. The changes of the solid phase were followed by X-ray diffraction and thermal analysis. Besides, pore-solution was expressed by application of high mechanical pressure (500 MPa) during different periods of the reaction in order to study its Chemical composition evolution as a result of the hydration process.
Reactivity of high alumina cement in water: Pore solution and solid phase characterization
M. T. Gaztañaga (Autor:in) / S. Goñi (Autor:in) / J. L. Sagrera (Autor:in)
1992
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
| British Library Online Contents | 1994
The pore solution phase of carbonated cement pastes
| British Library Online Contents | 2005
The pore solution phase of carbonated cement pastes
| Online Contents | 2005