Facile Synthesis of MOFs-Templated Carbon Aerogels with Enhanced Tetracycline Adsorption Performance
Three-dimensional aerogels have great potential for antibiotic removal from aqueous solution due to their excellent solution mass transfer channels and special morphology. Herein, the metal ions were bound with alginate to form alginate-Fe, alginate-Cu, and alginate-Fe-Cu hydrogels, then they were used as nucleation sites for metal organic framework (MOF) growth to obtain MAlgs gels, respectively. Considering the aqueous environmental stability of MOFs particles, the alginate and MOF particles in MAlgs aerogels were pyrolyzed as templates to obtain the derived carbon aerogel CMAlgs. The results showed that the adsorption capacity of MAlgs-Fe-Cu aerogel was higher than that of MAlg-Cu and MAlg-Fe aerogels, up to ~130 mg·g−1. The adsorption performance of carbon aerogel CMAlg-Cu decreased obviously because of the decrease of pore size and oxygen-containing functional groups. The adsorption process is a combination of physical adsorption and chemical adsorption. In addition, CMAlgs aerogels exhibit better recyclability than MAlgs aerogels. This work provides a new strategy for fabricating MOFs-templated in-situ grown carbon aerogels for water purification.
Facile Synthesis of MOFs-Templated Carbon Aerogels with Enhanced Tetracycline Adsorption Performance
Three-dimensional aerogels have great potential for antibiotic removal from aqueous solution due to their excellent solution mass transfer channels and special morphology. Herein, the metal ions were bound with alginate to form alginate-Fe, alginate-Cu, and alginate-Fe-Cu hydrogels, then they were used as nucleation sites for metal organic framework (MOF) growth to obtain MAlgs gels, respectively. Considering the aqueous environmental stability of MOFs particles, the alginate and MOF particles in MAlgs aerogels were pyrolyzed as templates to obtain the derived carbon aerogel CMAlgs. The results showed that the adsorption capacity of MAlgs-Fe-Cu aerogel was higher than that of MAlg-Cu and MAlg-Fe aerogels, up to ~130 mg·g−1. The adsorption performance of carbon aerogel CMAlg-Cu decreased obviously because of the decrease of pore size and oxygen-containing functional groups. The adsorption process is a combination of physical adsorption and chemical adsorption. In addition, CMAlgs aerogels exhibit better recyclability than MAlgs aerogels. This work provides a new strategy for fabricating MOFs-templated in-situ grown carbon aerogels for water purification.
Facile Synthesis of MOFs-Templated Carbon Aerogels with Enhanced Tetracycline Adsorption Performance
Yan Kong (Autor:in) / Kun Han (Autor:in) / Yuan Zhuang (Autor:in) / Baoyou Shi (Autor:in)
2022
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
| British Library Online Contents | 2019
Mechanically strong ice-templated laponite/poly(vinyl alcohol) aerogels
| British Library Online Contents | 2015
Facile synthesis of vanadia aerogels with controlled V3+/V4+ ratio
| British Library Online Contents | 2015
A facile method to prepare carbon aerogels from amphiphilic carbon material
| British Library Online Contents | 2012