The effect of using hybrid nanomaterials on drying shrinkage and strength of cement pastes
The aim of this work is to study the effect of nanomaterials on the properties of cement paste, the experimental program included three parts: a- two types of nanosilica, locally produced NS1 and imported NS2, b- nanoclay (NC) and c- Hybrid nanoparticles (NS1 & NC). In each part, cement paste was used with different percentages of nanoparticles. Compressive strength and drying shrinkage tests were applied in each part on the cured and uncured samples. The results showed that the compressive strength improved in the cement paste mixtures in the cured condition, the optimum percentages was 1% for NS1, 1% for NS2, 5% for NC, and 5% (0.5%NS1 & 4.5%NC) for hybrid nanoparticles. The drying shrinkage increases with adding nanosilica and hybrid nanoparticles, while it decreases when adding NC.
The effect of using hybrid nanomaterials on drying shrinkage and strength of cement pastes
The aim of this work is to study the effect of nanomaterials on the properties of cement paste, the experimental program included three parts: a- two types of nanosilica, locally produced NS1 and imported NS2, b- nanoclay (NC) and c- Hybrid nanoparticles (NS1 & NC). In each part, cement paste was used with different percentages of nanoparticles. Compressive strength and drying shrinkage tests were applied in each part on the cured and uncured samples. The results showed that the compressive strength improved in the cement paste mixtures in the cured condition, the optimum percentages was 1% for NS1, 1% for NS2, 5% for NC, and 5% (0.5%NS1 & 4.5%NC) for hybrid nanoparticles. The drying shrinkage increases with adding nanosilica and hybrid nanoparticles, while it decreases when adding NC.
The effect of using hybrid nanomaterials on drying shrinkage and strength of cement pastes
Saaid I. Zaki (Autor:in) / Hossam A. Hodhod (Autor:in) / Mostafa A. Mahdi (Autor:in)
2016
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Drying shrinkage of ordinary portland cement pastes
| Tema Archiv | 1989
Effect of Metakaolin on the Drying Shrinkage Behaviour of Portland Cement Pastes
| Springer Verlag | 2015
Relationship Between the Microstructure, Composition and Drying Shrinkage of Cement Pastes
| British Library Online Contents | 2005
Autogenous Shrinkage of Various Cement Pastes
| British Library Conference Proceedings | 1993
Shrinkage of hardened portland cement pastes
| TIBKAT | 1969