Properties of Wood Ceramics Prepared from Thermo-Modified Poplar
Wood ceramics (WCS) were prepared from thermo-modified poplar wood residues and untreated poplar wood. At 1000 °C sintering temperature, the ratios of wood powder and phenolic resin at 10:3, 10:6 and 10:9 were tested. The effects of materials on the properties of WCS, carbon yield and volume shrinkage were studied. With the increase in resin content, the carbon yield increased; however, the volume shrinkage decreased. Carbon yield of WCS made from 220 °C thermo-modified poplar wood was 40.45%, as the ratio of wood powder/phenolic resins was 10:6. The microstructure, chemical structure and crystallinity of WCS were analysed by scanning electron microscopy (SEM), Fourier transform infrared (FT-IR) and X-ray diffraction (XRD), respectively. The results showed that WCS had a porous structure. WCS prepared from thermo-modified materials, amorphous carbon and hard glass carbon melted more evenly; meanwhile, there were more pores on glass carbon. The FTIR spectra showed that the stretching vibration of C-O-C weakened at ceramics made of thermo-modified poplar. The XRD pattern indicated that the raw material has no apparent influence on the graphitization degree of WCS.
Properties of Wood Ceramics Prepared from Thermo-Modified Poplar
Wood ceramics (WCS) were prepared from thermo-modified poplar wood residues and untreated poplar wood. At 1000 °C sintering temperature, the ratios of wood powder and phenolic resin at 10:3, 10:6 and 10:9 were tested. The effects of materials on the properties of WCS, carbon yield and volume shrinkage were studied. With the increase in resin content, the carbon yield increased; however, the volume shrinkage decreased. Carbon yield of WCS made from 220 °C thermo-modified poplar wood was 40.45%, as the ratio of wood powder/phenolic resins was 10:6. The microstructure, chemical structure and crystallinity of WCS were analysed by scanning electron microscopy (SEM), Fourier transform infrared (FT-IR) and X-ray diffraction (XRD), respectively. The results showed that WCS had a porous structure. WCS prepared from thermo-modified materials, amorphous carbon and hard glass carbon melted more evenly; meanwhile, there were more pores on glass carbon. The FTIR spectra showed that the stretching vibration of C-O-C weakened at ceramics made of thermo-modified poplar. The XRD pattern indicated that the raw material has no apparent influence on the graphitization degree of WCS.
Properties of Wood Ceramics Prepared from Thermo-Modified Poplar
Hongyan Chen (Autor:in) / Mohsen Bahmani (Autor:in) / Miha Humar (Autor:in) / Dali Cheng (Autor:in)
2020
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
WCS , thermo-modified wood , SEM , XRD , FTIR , Plant ecology , QK900-989
Metadata by DOAJ is licensed under CC BY-SA 1.0
Dynamic Mechanical Properties of Trimethylborate (TMB) Modified Poplar Wood by Sol-Gel Process
| British Library Conference Proceedings | 2013
Dynamic Mechanical Properties of Trimethylborate (TMB) Modified Poplar Wood by Sol-Gel Process
| Trans Tech Publications | 2013
Alkaline treatment of poplar wood
| British Library Online Contents | 1999
Thermally Compressed Poplar Wood (TCW): Physical and Mechanical Properties
| BASE | 2013
Antibacterial property of titanium alkoxide/poplar wood composite prepared by sol–gel process
| British Library Online Contents | 2012