Properties of pervious concrete with various types and sizes of aggregate
The benefit of pervious concrete lies in its ability to transport a large volume of water through its pores to the underlying strata, and it often serves as a pavement for vehicles and pedestrians. This research aimed to determine the properties of pervious concrete based on trials in the laboratory. The method used in this research was a laboratory experiment in accordance with the appropriate standards. The local material used in the mixture was a material composition with Portland Cement Composite with a water-cement (W/C) ratio 0.27 to 0.34, with aggregates of various types and sizes and fly ash and superplasticizer as the added ingredients. The mixture for the trial used 4.25 for the aggregatecement ratio (A/C) with a proportion of 6% for the fine aggregate (sand), 15% flay ash and a low dosage of superplastizer. The test results showed a slight difference in compressive strength and split tensile strength alongside variations in the W/C, including the use of different aggregate types and sizes. The permeability when using natural aggregate was more porous compared to the crushed stone. The effect of the aggregate size from small to large will result in decreased density (unit weight) and increased void in the mixture. Good agreement was reached in the 0.30 wcr mixture with an aggregate size that passed through a 12.5 mm sieve, that was retained at 9.5 mm and that provided suitable compressive strength.
Properties of pervious concrete with various types and sizes of aggregate
The benefit of pervious concrete lies in its ability to transport a large volume of water through its pores to the underlying strata, and it often serves as a pavement for vehicles and pedestrians. This research aimed to determine the properties of pervious concrete based on trials in the laboratory. The method used in this research was a laboratory experiment in accordance with the appropriate standards. The local material used in the mixture was a material composition with Portland Cement Composite with a water-cement (W/C) ratio 0.27 to 0.34, with aggregates of various types and sizes and fly ash and superplasticizer as the added ingredients. The mixture for the trial used 4.25 for the aggregatecement ratio (A/C) with a proportion of 6% for the fine aggregate (sand), 15% flay ash and a low dosage of superplastizer. The test results showed a slight difference in compressive strength and split tensile strength alongside variations in the W/C, including the use of different aggregate types and sizes. The permeability when using natural aggregate was more porous compared to the crushed stone. The effect of the aggregate size from small to large will result in decreased density (unit weight) and increased void in the mixture. Good agreement was reached in the 0.30 wcr mixture with an aggregate size that passed through a 12.5 mm sieve, that was retained at 9.5 mm and that provided suitable compressive strength.
Properties of pervious concrete with various types and sizes of aggregate
Mulyono Tri (Autor:in) / Anisah (Autor:in)
2019
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
| Taylor & Francis Verlag | 2024
| Taylor & Francis Verlag | 2024
| British Library Online Contents | 2016
Pervious Concrete: Compaction and Aggregate Gradation
| British Library Online Contents | 2009